Thermal shock behavior of porous Si3N4 ceramics with Nd(2)O(3 )as sintering additive
文献类型:期刊论文
作者 | Liang, Hanqin; Yin, Jinwei; Zuo, Kaihui; Xia, Yongfeng; Yao, Dongxu; Zeng, Yuping |
刊名 | INTERNATIONAL JOURNAL OF APPLIED CERAMIC TECHNOLOGY |
出版日期 | 2019-07-01 |
卷号 | 16期号:4页码:1390 |
ISSN号 | 1546-542X |
关键词 | Nd2O3 oxidation Si3N4 thermal shock |
DOI | 10.1111/ijac.13197 |
文献子类 | Article |
英文摘要 | The thermal shock behavior of porous Si(3)N(4 )ceramics with Nd2O3 as sintering additive was investigated by the water quenching method in the temperature difference range from 200 to 1500 degrees C. The porosity and residual flexural strength of the specimens after single water quenching were measured to reveal the influence of thermal shock on porous Si3N4 ceramics. It was found that the critical temperature was 780 degrees C, which was almost 230 degrees C higher than its dense counterpart reported by other researchers. Scanning electron microscope was used to examine the microstructure evolution of the external surface and interior after water quenching. Surface oxidation and cracks formation were found to be the primary cause of the strength degradation of porous Si3N4 ceramics. The phase composition variation in the surface was also characterized by X-ray diffraction. |
WOS研究方向 | Materials Science |
语种 | 英语 |
出版者 | WILEY |
源URL | [http://ir.sic.ac.cn/handle/331005/27015] |
专题 | 中国科学院上海硅酸盐研究所 |
推荐引用方式 GB/T 7714 | Liang, Hanqin,Yin, Jinwei,Zuo, Kaihui,et al. Thermal shock behavior of porous Si3N4 ceramics with Nd(2)O(3 )as sintering additive[J]. INTERNATIONAL JOURNAL OF APPLIED CERAMIC TECHNOLOGY,2019,16(4):1390. |
APA | Liang, Hanqin,Yin, Jinwei,Zuo, Kaihui,Xia, Yongfeng,Yao, Dongxu,&Zeng, Yuping.(2019).Thermal shock behavior of porous Si3N4 ceramics with Nd(2)O(3 )as sintering additive.INTERNATIONAL JOURNAL OF APPLIED CERAMIC TECHNOLOGY,16(4),1390. |
MLA | Liang, Hanqin,et al."Thermal shock behavior of porous Si3N4 ceramics with Nd(2)O(3 )as sintering additive".INTERNATIONAL JOURNAL OF APPLIED CERAMIC TECHNOLOGY 16.4(2019):1390. |
入库方式: OAI收割
来源:上海硅酸盐研究所
浏览0
下载0
收藏0
其他版本
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。