The improved mechanical properties of Al matrix composites reinforced with oriented beta-Si3N4 whisker
文献类型：期刊论文
| 作者 | Zhang, Chenxu; Zeng, Yu-Ping; Yao, Dongxu; Yin, Jinwei; Zuo, Kaihui; Xia, Yongfeng; Liang, Hanqin |
| 刊名 | JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY
 |
| 出版日期 | 2019-07-01 |
| 卷号 | 35期号:7页码:1345 |
| 关键词 | Metal-matrix composites (MMC) beta-Si3N4 whiskers Preferred orientation Interface Mechanical properties Extrusion |
| ISSN号 | 1005-0302 |
| DOI | 10.1016/j.jmst.2019.02.003 |
| 文献子类 | Article |
| 英文摘要 | The beta-Si3N4 whiskers (beta-Si(3)N(4)w) reinforced Al matrix composites were first fabricated by hot pressing, then treated through hot extrusion. The microstructure characterization demonstrated the preferred orientations of both beta-Si(3)N(4)w and Al grains in the as-extruded composites. It indicated that beta-Si(3)N(4)w were aligned along the extrusion direction and Al grains exhibited a distinct <111>(Al) texture. The interface between beta-Si(3)N(4)w and Al was in a good bonding status without voids and reaction products. Effects of extrusion process on the mechanical properties of composites were also investigated. The results indicated the extrusion process had a prominent strengthening effect on the mechanical properties of composites. The maximum yield strength and ultimate tensile strength of composites reached up to 170 and 289 MPa, respectively, accompanied by a 12.3% elongation at fracture when the whisker fraction was 15 vol.%. This improvement was collectively attributed to the densification of composites, the strong interface, and the preferred orientation inside composites. The yield strength of the composites reinforced with 5 vol.% beta-Si(3)N(4)w corresponded well with the theoretical value from different strengthening mechanisms. (C) 2019 Published by Elsevier Ltd on behalf of The editorial office of Journal of Materials Science & Technology. |
| WOS研究方向 | Materials Science ; Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| 出版者 | JOURNAL MATER SCI TECHNOL |
| 源URL | [http://ir.sic.ac.cn/handle/331005/27026]  |
| 专题 | 中国科学院上海硅酸盐研究所 |
| 推荐引用方式 GB/T 7714 | Zhang, Chenxu,Zeng, Yu-Ping,Yao, Dongxu,et al. The improved mechanical properties of Al matrix composites reinforced with oriented beta-Si3N4 whisker[J]. JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY,2019,35(7):1345. |
| APA | Zhang, Chenxu.,Zeng, Yu-Ping.,Yao, Dongxu.,Yin, Jinwei.,Zuo, Kaihui.,...&Liang, Hanqin.(2019).The improved mechanical properties of Al matrix composites reinforced with oriented beta-Si3N4 whisker.JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY,35(7),1345. |
| MLA | Zhang, Chenxu,et al."The improved mechanical properties of Al matrix composites reinforced with oriented beta-Si3N4 whisker".JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY 35.7(2019):1345. |
入库方式： OAI收割
来源：上海硅酸盐研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。