Dual Substitution and Spark Plasma Sintering to Improve Ionic Conductivity of Garnet Li7La3Zr2O12
文献类型：期刊论文
| 作者 | Dong, Zhencai; Xu, Chao; Wu, Yongmin; Tang, Weiping; Song, Shufeng; Yao, Jianyao; Huang, Zhengyong; Wen, Zhaoyin; Lu, Li; Hu, Ning |
| 刊名 | NANOMATERIALS
 |
| 出版日期 | 2019-05-01 |
| 卷号 | 9期号:5 |
| 关键词 | garnet dual substitution spark plasma sintering conductivity |
| ISSN号 | 2079-4991 |
| DOI | 10.3390/nano9050721 |
| 文献子类 | Article |
| 英文摘要 | Garnet Li7La3Zr2O12 is one of the most promising solid electrolytes used for solid-state lithium batteries. However, low ionic conductivity impedes its application. Herein, we report Ta-doping garnets with compositions of Li7-xLa3Zr2-xTaxO12 (0.1 <= x <= 0.75) obtained by solid-state reaction and free sintering, which was facilitated by graphene oxide (GO). Furthermore, to optimize Li6.6La3Zr1.6Ta0.4O12, Mg2+ was select as a second dopant. The dual substitution of Ta5+ for Zr4+ and Mg2+ for Li+ with a composition of Li6.5Mg0.05La3Zr1.6Ta0.4O12 showed an enhanced total ionic conductivity of 6.1 x 10(-4) S cm(-1) at room temperature. Additionally, spark plasma sintering (SPS) was applied to further densify the garnets and enhance their ionic conductivities. Both SPS specimens present higher conductivities than those produced by the conventional free sintering. At room temperature, the highest ionic conductivity of Li6.5Mg0.05La3Zr1.6Ta0.4O12 sintered at 1000 degrees C is 8.8 x 10(-4) S cm(-1), and that of Li6.6La3Zr1.6Ta0.4O12 sintered at 1050 degrees C is 1.18 x 10(-3) S cm(-1). |
| WOS研究方向 | Science & Technology - Other Topics ; Materials Science |
| 语种 | 英语 |
| 出版者 | MDPI |
| 源URL | [http://ir.sic.ac.cn/handle/331005/27127]  |
| 专题 | 中国科学院上海硅酸盐研究所 |
| 推荐引用方式 GB/T 7714 | Dong, Zhencai,Xu, Chao,Wu, Yongmin,et al. Dual Substitution and Spark Plasma Sintering to Improve Ionic Conductivity of Garnet Li7La3Zr2O12[J]. NANOMATERIALS,2019,9(5). |
| APA | Dong, Zhencai.,Xu, Chao.,Wu, Yongmin.,Tang, Weiping.,Song, Shufeng.,...&Hu, Ning.(2019).Dual Substitution and Spark Plasma Sintering to Improve Ionic Conductivity of Garnet Li7La3Zr2O12.NANOMATERIALS,9(5). |
| MLA | Dong, Zhencai,et al."Dual Substitution and Spark Plasma Sintering to Improve Ionic Conductivity of Garnet Li7La3Zr2O12".NANOMATERIALS 9.5(2019). |
入库方式： OAI收割
来源：上海硅酸盐研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。