Organosilicon chains strengthened flexible graphene aerogel with improved compression modulus and tunable functionality
文献类型：期刊论文
| 作者 | Li, Jingjing; Zhong, He; Zhang, Jingxian; Li, Xiaoguang; Duan, Yusen; Jiang, Dongliang |
| 刊名 | DIAMOND AND RELATED MATERIALS
 |
| 出版日期 | 2019-05-01 |
| 卷号 | 95页码:91 |
| ISSN号 | 0925-9635 |
| 关键词 | Graphene aerogel Tetraethyl orthosilicate Mechanical strength Compression modulus Adsorption capacity |
| DOI | 10.1016/j.diamond.2019.04.005 |
| 文献子类 | Article |
| 英文摘要 | The idea of increasing the mechanical strength of graphene aerogel (GA) and achieving more reliable application performance has aroused wide attention recently. A solution to this challenge is to reinforce the framework of aerogel by adding enhancers to the initial graphene oxide (GO) solution. Herein, organosilicon chains strengthened compressible GA was fabricated in a facile and low-cost method by introducing tetraethyl orthosilicate (TEOS) as the reinforce agent. The effects of TEOS on the porous microstructure and mechanical properties of GA were systematically studied, and the best mechanical performance obtained at the mass ratio of TEOS to GO equal to 3:1. The final well-structured TEOS-3 aerogel exhibits a maximum compression modulus of 29 kPa, which is higher than that reported in previous works. In addition, it showed an excellent hydrophobicity (contact angle, 131.71 degrees), a high adsorption capacity (72 times of its own weight) and excellent regeneration capacity for toluene, a good electrical conductivity of similar to 0.1 S-m(-1) and a low density of 15.56 mg.cm(-3). This work might provide hints for the large-scale preparation and practical application of graphene aerogel with more reliable application performance. |
| WOS研究方向 | Materials Science ; Physics |
| 语种 | 英语 |
| 出版者 | ELSEVIER SCIENCE SA |
| 源URL | [http://ir.sic.ac.cn/handle/331005/27135]  |
| 专题 | 中国科学院上海硅酸盐研究所 |
| 推荐引用方式 GB/T 7714 | Li, Jingjing,Zhong, He,Zhang, Jingxian,et al. Organosilicon chains strengthened flexible graphene aerogel with improved compression modulus and tunable functionality[J]. DIAMOND AND RELATED MATERIALS,2019,95:91. |
| APA | Li, Jingjing,Zhong, He,Zhang, Jingxian,Li, Xiaoguang,Duan, Yusen,&Jiang, Dongliang.(2019).Organosilicon chains strengthened flexible graphene aerogel with improved compression modulus and tunable functionality.DIAMOND AND RELATED MATERIALS,95,91. |
| MLA | Li, Jingjing,et al."Organosilicon chains strengthened flexible graphene aerogel with improved compression modulus and tunable functionality".DIAMOND AND RELATED MATERIALS 95(2019):91. |
入库方式： OAI收割
来源：上海硅酸盐研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。