Metal-Organic Frameworks as Electrolyte Additives To Enable Ultrastable Plating/Stripping of Li Anode with Dendrite Inhibition
文献类型：期刊论文
| 作者 | Chu, Fulu; Hu, Jiulin; Wu, Chenglong; Yao, Zhenguo; Tian, Jing; Li, Zheng; Li, Chilin |
| 刊名 | ACS APPLIED MATERIALS & INTERFACES
 |
| 出版日期 | 2019-01-30 |
| 卷号 | 11期号:4页码:3869 |
| 关键词 | electrolyte additive metal-organic framework UiO-66 Li dendrite suppression Li metal batteries |
| ISSN号 | 1944-8244 |
| DOI | 10.1021/acsami.8b17924 |
| 文献子类 | Article |
| 英文摘要 | Suppressing the extrusion of Li dendrites and alleviating the volume expansion of Li anode during long-term cycling are of great significance to achieve highly reversible Li metal batteries of high energy density potential. However, the exploration of facile and effective solutions to smoothen anode surface is still a big challenge. Here, we propose a solid additive strategy by blending tailored metal-organic framework (MOF) grains with typical carbonate electrolyte to enable an ultrastable plating/stripping cycling of Li anode for at least 1400 h with evident inhibition of anode roughening and voltage polarization. Zr-based MOF (UiO-66) additive enables the smallest nucleation and plateau ocverpotentials (similar to 80 mV) during Li plating especially under high current density (2 mA/cm(2)) and large areal capacity (4 mAh/cm(2)). The kinetic and cyclic advantages of Li anode modulated by UiO-66 not only benefit from its intrinsic features (high surface area/porosity and thermal/electrochemical stability) but also from the reinforced solid electrolyte interface with low resistance, which consists of concentrated LiF and robust Zr-O-C moieties. Li-Li4Ti50O12 cell based on MOF additive can achieve a high reversibility for at least 900 cycles. |
| WOS研究方向 | Science & Technology - Other Topics ; Materials Science |
| 语种 | 英语 |
| 出版者 | AMER CHEMICAL SOC |
| 源URL | [http://ir.sic.ac.cn/handle/331005/27379]  |
| 专题 | 中国科学院上海硅酸盐研究所 |
| 推荐引用方式 GB/T 7714 | Chu, Fulu,Hu, Jiulin,Wu, Chenglong,et al. Metal-Organic Frameworks as Electrolyte Additives To Enable Ultrastable Plating/Stripping of Li Anode with Dendrite Inhibition[J]. ACS APPLIED MATERIALS & INTERFACES,2019,11(4):3869. |
| APA | Chu, Fulu.,Hu, Jiulin.,Wu, Chenglong.,Yao, Zhenguo.,Tian, Jing.,...&Li, Chilin.(2019).Metal-Organic Frameworks as Electrolyte Additives To Enable Ultrastable Plating/Stripping of Li Anode with Dendrite Inhibition.ACS APPLIED MATERIALS & INTERFACES,11(4),3869. |
| MLA | Chu, Fulu,et al."Metal-Organic Frameworks as Electrolyte Additives To Enable Ultrastable Plating/Stripping of Li Anode with Dendrite Inhibition".ACS APPLIED MATERIALS & INTERFACES 11.4(2019):3869. |
入库方式： OAI收割
来源：上海硅酸盐研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。