Effect of (Tb plus Y)/Al ratio on Microstructure Evolution and Densification Process of (Tb0.6Y0.4)(3)Al5O12 Transparent Ceramics
文献类型：期刊论文
| 作者 | Wan, Zhong; Wang, Yinzhen; Zhang, Jian; Wang, Shiwei; Han, Dan; Wang, Junping; Wang, Dewen |
| 刊名 | MATERIALS
 |
| 出版日期 | 2019-01-02 |
| 卷号 | 12期号:2 |
| 关键词 | (Tb0.6Y0.4)(3)Al5O12 densification process grain growth HIP treatment |
| ISSN号 | 1996-1944 |
| DOI | 10.3390/ma12020300 |
| 文献子类 | Article |
| 英文摘要 | (Tb0.6Y0.4)(3)Al5O12 transparent ceramics were successfully fabricated by solid-state reactive sintering using Tb4O7, Y2O3, and -Al2O3 powders as raw materials. The effect of (Tb+Y)/Al ratio on microstructure evolution and densification process was investigated in detailed. The results showed that the grain growth kinetics were significantly affected by (Tb+Y)/Al ratio. Al-rich and Tb-rich phases appeared in part of the samples of different ratios. Particularly, excess aluminum increased the diffusing process, leading to a higher densification rate, while samples with excess terbium ratios displayed a smaller grain size and lower relative density. The optical quality was highly related to the amount of the secondary phase produced by different (Tb+Y)/Al ratios. Finally, (Tb0.6Y0.4)(3)Al5O12 transparent ceramics have been fabricated through pre-sintering in vacuum, followed by hot isostatic sintering (HIP), and the best transmittance of sample with a 4 mm thickness was approximately 78% at 1064 nm. |
| WOS研究方向 | Materials Science |
| 语种 | 英语 |
| 出版者 | MDPI |
| 源URL | [http://ir.sic.ac.cn/handle/331005/27408]  |
| 专题 | 中国科学院上海硅酸盐研究所 |
| 推荐引用方式 GB/T 7714 | Wan, Zhong,Wang, Yinzhen,Zhang, Jian,et al. Effect of (Tb plus Y)/Al ratio on Microstructure Evolution and Densification Process of (Tb0.6Y0.4)(3)Al5O12 Transparent Ceramics[J]. MATERIALS,2019,12(2). |
| APA | Wan, Zhong.,Wang, Yinzhen.,Zhang, Jian.,Wang, Shiwei.,Han, Dan.,...&Wang, Dewen.(2019).Effect of (Tb plus Y)/Al ratio on Microstructure Evolution and Densification Process of (Tb0.6Y0.4)(3)Al5O12 Transparent Ceramics.MATERIALS,12(2). |
| MLA | Wan, Zhong,et al."Effect of (Tb plus Y)/Al ratio on Microstructure Evolution and Densification Process of (Tb0.6Y0.4)(3)Al5O12 Transparent Ceramics".MATERIALS 12.2(2019). |
入库方式： OAI收割
来源：上海硅酸盐研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。