Corrosion behavior of alumina-based ceramic core materials in caustic alkali solutions
文献类型:期刊论文
作者 | Gao, Zhao-Fen; Wang, Bao-Quan; Yin, Jinwei; Zeng, Yu-Ping |
刊名 | INTERNATIONAL JOURNAL OF APPLIED CERAMIC TECHNOLOGY
![]() |
出版日期 | 2019 |
卷号 | 16期号:1页码:335 |
关键词 | ceramic core corrosion mass loss |
ISSN号 | 1546-542X |
DOI | 10.1111/ijac.13053 |
文献子类 | Article |
英文摘要 | Corrosion behaviors of the porous alumina-based ceramic core materials in KOH and NaOH solution were investigated. Corrosion tests were carried out at 100 degrees C, 150 degrees C, and 200 degrees C, and the concentration of KOH and NaOH was 50, 67, and 75 wt%, respectively. The results indicated that the optimal concentration was 67 wt% for KOH solution and 50 wt% for NaOH solution, respectively. Increasing corrosion temperature and prolonging corrosion time were helpful to enhance the corrosion effect, and temperature played an extra important role during the whole corrosion process. NaOH solution was better than KOH solution for corrosion at the same temperature and concentration. |
WOS研究方向 | Materials Science |
语种 | 英语 |
出版者 | WILEY |
源URL | [http://ir.sic.ac.cn/handle/331005/27410] ![]() |
专题 | 中国科学院上海硅酸盐研究所 |
推荐引用方式 GB/T 7714 | Gao, Zhao-Fen,Wang, Bao-Quan,Yin, Jinwei,et al. Corrosion behavior of alumina-based ceramic core materials in caustic alkali solutions[J]. INTERNATIONAL JOURNAL OF APPLIED CERAMIC TECHNOLOGY,2019,16(1):335. |
APA | Gao, Zhao-Fen,Wang, Bao-Quan,Yin, Jinwei,&Zeng, Yu-Ping.(2019).Corrosion behavior of alumina-based ceramic core materials in caustic alkali solutions.INTERNATIONAL JOURNAL OF APPLIED CERAMIC TECHNOLOGY,16(1),335. |
MLA | Gao, Zhao-Fen,et al."Corrosion behavior of alumina-based ceramic core materials in caustic alkali solutions".INTERNATIONAL JOURNAL OF APPLIED CERAMIC TECHNOLOGY 16.1(2019):335. |
入库方式: OAI收割
来源:上海硅酸盐研究所
浏览0
下载0
收藏0
其他版本
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。