C/SiOC Composites by a Modified PIP Using Solid Polysiloxane: Fabrication, Microstructure and Mechanical Properties
文献类型：期刊论文
| 作者 | Wu Qing-Qing; Wang Zhen; Ding Qi; Ni De-Wei; Kan Yan-Mei; Dong Shao-Ming |
| 刊名 | JOURNAL OF INORGANIC MATERIALS
 |
| 出版日期 | 2019-12-20 |
| 卷号 | 34期号:12页码:1349 |
| 关键词 | C/SiOC composite high-efficient PIP microstructure cross-linking mechanism |
| ISSN号 | 1000-324X |
| DOI | 10.15541/jim20190080 |
| 文献子类 | Article |
| 英文摘要 | A modified polymer infiltration and pyrolysis method (PIP) was developed to enhance the densification of C/SiOC composites, using molten MK resin (polymethylsilsesquioxane) as precursor. Organic sulfonic acid was added as cross-linking agent to lower the curing temperature. The cross-linking mechanism and ceramization behavior of MK resin was studied. A high ceramic yield of about 85wt% and low free carbon content below 3wt% are achieved, with excellent high-temperature stability of the derived SiOC. The modified PIP approach presents a high densification efficiency. After only 8 PIP cycles, the final C/SiOC composites possess a density of about 1.81 g/cm(3). Compared with those composites fabricated by conventional PIP process, the C/SiOC composites prepared by modified PIP process show a much denser microstructure with much more improved densification efficiency. Bending strength of the as-fabricated C/SiOC composites is of (312 +/- 25) MPa, showing obvious non-brittle fracture behavior. |
| WOS关键词 | C-F/SIOC COMPOSITES ; TEMPERATURE ; CERAMICS ; INFILTRATION ; EVOLUTION ; BEHAVIOR ; CARBON ; PYROLYSIS |
| WOS研究方向 | Materials Science |
| 语种 | 英语 |
| 出版者 | SCIENCE PRESS |
| 源URL | [http://ir.sic.ac.cn/handle/331005/27444]  |
| 专题 | 中国科学院上海硅酸盐研究所 |
| 推荐引用方式 GB/T 7714 | Wu Qing-Qing,Wang Zhen,Ding Qi,et al. C/SiOC Composites by a Modified PIP Using Solid Polysiloxane: Fabrication, Microstructure and Mechanical Properties[J]. JOURNAL OF INORGANIC MATERIALS,2019,34(12):1349. |
| APA | Wu Qing-Qing,Wang Zhen,Ding Qi,Ni De-Wei,Kan Yan-Mei,&Dong Shao-Ming.(2019).C/SiOC Composites by a Modified PIP Using Solid Polysiloxane: Fabrication, Microstructure and Mechanical Properties.JOURNAL OF INORGANIC MATERIALS,34(12),1349. |
| MLA | Wu Qing-Qing,et al."C/SiOC Composites by a Modified PIP Using Solid Polysiloxane: Fabrication, Microstructure and Mechanical Properties".JOURNAL OF INORGANIC MATERIALS 34.12(2019):1349. |
入库方式： OAI收割
来源：上海硅酸盐研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。