A novel thermosetting composite with excellent high-frequency dielectric properties and ultra-high-temperature resistance
文献类型:期刊论文
作者 | Huang, Yanchun; Peng, Haiyi; Zhang, Heng; Lin, Huixing; Deng, Shifeng; Yao, Xiaogang |
刊名 | JOURNAL OF MATERIALS SCIENCE-MATERIALS IN ELECTRONICS |
出版日期 | 2019-12-30 |
卷号 | 30期号:24页码:21495 |
ISSN号 | 0957-4522 |
DOI | 10.1007/s10854-019-02534-z |
文献子类 | Article |
英文摘要 | 0.8MgTiO(3) - 0.2(Ca0.7La0.2)TiO3 (MTCLT) ceramic fillers with excellent microwave dielectric properties have been incorporated in a novel polysilylaryl-enyne (PSAE) resin with low dielectric loss to prepare PSAE/MTCLT composite. A unique process free of organic solvent has been employed to fabricate the composite. The results showed that highly dense and homogeneous microstructure was observed in all the composites with different filler volume fractions. With the increase in MTCLT volume fraction, the dielectric constant of the composite increased significantly from 2.8 to 10.0, while the dielectric loss decreased from 0.0056 to 0.0030 at 10 GHz. The coefficient of thermal expansion (CTE) of the composite could be reduced to less than 20 ppm/degrees C when 40 V% MTCLT ceramic was loaded which achieved a good match with copper foil. TGA and DMA results showed that the composite possessed excellent temperature resistance with the temperature at 5% mass loss (T-d5)>850 degrees C and glass transition temperature (T-g)>400 degrees C at N-2 atmosphere. The novel thermosetting PSAE/MTCLT composite reported in this work has good application prospects in high-power integrated circuits and some high-temperature-resistant environments. |
WOS关键词 | POLYMER-CERAMIC COMPOSITES ; NANOCOMPOSITE FILMS ; CONSTANT ; FABRICATION |
WOS研究方向 | Engineering ; Materials Science ; Physics |
语种 | 英语 |
出版者 | SPRINGER |
源URL | [http://ir.sic.ac.cn/handle/331005/27461] |
专题 | 中国科学院上海硅酸盐研究所 |
推荐引用方式 GB/T 7714 | Huang, Yanchun,Peng, Haiyi,Zhang, Heng,et al. A novel thermosetting composite with excellent high-frequency dielectric properties and ultra-high-temperature resistance[J]. JOURNAL OF MATERIALS SCIENCE-MATERIALS IN ELECTRONICS,2019,30(24):21495. |
APA | Huang, Yanchun,Peng, Haiyi,Zhang, Heng,Lin, Huixing,Deng, Shifeng,&Yao, Xiaogang.(2019).A novel thermosetting composite with excellent high-frequency dielectric properties and ultra-high-temperature resistance.JOURNAL OF MATERIALS SCIENCE-MATERIALS IN ELECTRONICS,30(24),21495. |
MLA | Huang, Yanchun,et al."A novel thermosetting composite with excellent high-frequency dielectric properties and ultra-high-temperature resistance".JOURNAL OF MATERIALS SCIENCE-MATERIALS IN ELECTRONICS 30.24(2019):21495. |
入库方式: OAI收割
来源:上海硅酸盐研究所
浏览0
下载0
收藏0
其他版本
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。