Chemical modification of electrospun yttrium silicate fiber with self-healing properties

文献类型:期刊论文

AuthorLi, Q. K.; Wang, C. H.; Pan, H.; Wang, Y. H.; Lin, W.; Li, G. S.; Wang, C. Q.; Wang, L.; Wang, Y.
SourceJOURNAL OF SOL-GEL SCIENCE AND TECHNOLOGY
Issued Date2019-12-31
ISSN0928-0707
KeywordYttrium silicate fiber Electrospinning Environmental barrier coating Self-healing
DOI10.1007/s10971-019-05188-9
SubtypeArticle; Early Access
English AbstractYttrium silicate is promising materials for the environmental barrier coatings. In this paper, yttrium silicate fiber was successfully prepared by electrostatic spinning, and the microstructure of yttrium silicate fibers was modified by the titanium silicide to improve densification degree of the fiber. In this study, the colloids were obtained by using yttrium nitrate and ethyl orthosilicate as the main raw materials, and the processes such as time and high-temperature calcination were researched. Moreover, the yttrium silicate fibers with different morphologies were obtained by using different proportions of different temperatures and adding different amounts of titanium silicide. The characterization methods such as TG-DSC, SEM, and XRD were used to investigate the preparation process of yttrium silicate fibers. The results show that the temperature has a great effect on the composition of compounds and the morphology of yttrium silicate fibers. The yttrium silicate fiber has the best structure with 15% mixing amount of titanium silicide. Left four figures were SEM images of yttrium silicate fibers calcined at (a) 1373 K (b) 1473 K (c) 1573 K (d) 1673K, and right four figures were SEM images of yttrium silicate fibers mixing 15% TiSi2 calcined at (a) 1373 K (b) 1473 K (c) 1573 K (d) 1673K [GRAPHICS] .
WOS KeywordOXIDATION PROTECTION ; NANOFIBERS ; COATINGS ; BETA-Y2SI2O7 ; FABRICATION ; RESISTANCE ; MEMBRANE ; TIO2
WOS Research AreaMaterials Science
Language英语
PublisherSPRINGER
源URL[http://ir.sic.ac.cn/handle/331005/27474]  
Collection中国科学院上海硅酸盐研究所
Recommended Citation
GB/T 7714
Li, Q. K.,Wang, C. H.,Pan, H.,et al. Chemical modification of electrospun yttrium silicate fiber with self-healing properties[J]. JOURNAL OF SOL-GEL SCIENCE AND TECHNOLOGY,2019.
APA Li, Q. K..,Wang, C. H..,Pan, H..,Wang, Y. H..,Lin, W..,...&Wang, Y..(2019).Chemical modification of electrospun yttrium silicate fiber with self-healing properties.JOURNAL OF SOL-GEL SCIENCE AND TECHNOLOGY.
MLA Li, Q. K.,et al."Chemical modification of electrospun yttrium silicate fiber with self-healing properties".JOURNAL OF SOL-GEL SCIENCE AND TECHNOLOGY (2019).

入库方式: OAI收割

来源:上海硅酸盐研究所

浏览0
下载0
收藏0
其他版本

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.