effectofga3dopingontheelectricalconductivityofnanosizedzincoxidepowders
文献类型：期刊论文
| 作者 | Du SF(杜尚丰); Gao WM(高卫民); Liu J(刘建); Chen YF(陈运法) ; Liang Y(梁云)
|
| 刊名 | raremetalmaterialsandengineering
 |
| 出版日期 | 2006 |
| 卷号 | 35期号:7页码:1139 |
| ISSN号 | 1002-185X |
| 英文摘要 | Highly electro-conductive nano-sized zinc oxide powders were prepared by calcining the precursor synthesized from ZnSO4 center dot 7H(2)O, GaCl3 and NH4HCO3 by the co-precipitation method. The obtained zinc oxide powders were characterized by SEM, TEM, XRD, XPS and BET techniques, and the influence of Ga3+ doping on the electrical conductivity of zinc oxide was investigated. It was found that the volume resistivity of the zinc oxide decreases to 2.0 Omega(.)cm when the Ga3+ doping content is 2.2 mol%, much lower than the conventional zinc oxide powders. This material can be effectively used as electro-conductive fillers in ceramics, fibers, dopes, rubbers and other fields. |
| 语种 | 英语 |
| 源URL | [http://ir.ipe.ac.cn/handle/122111/34782]  |
| 专题 | 中国科学院过程工程研究所 |
| 作者单位 | 中国科学院过程工程研究所 |
| 推荐引用方式 GB/T 7714 | Du SF,Gao WM,Liu J,et al. effectofga3dopingontheelectricalconductivityofnanosizedzincoxidepowders[J]. raremetalmaterialsandengineering,2006,35(7):1139. |
| APA | 杜尚丰,高卫民,刘建,陈运法,&梁云.(2006).effectofga3dopingontheelectricalconductivityofnanosizedzincoxidepowders.raremetalmaterialsandengineering,35(7),1139. |
| MLA | 杜尚丰,et al."effectofga3dopingontheelectricalconductivityofnanosizedzincoxidepowders".raremetalmaterialsandengineering 35.7(2006):1139. |
入库方式： OAI收割
来源：过程工程研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。