前驱体热解氮化硼碳化硅复相泡沫陶瓷的抗氧化与高温隔热性能研究
文献类型：期刊论文
| 作者 | 沈志洵; 戈敏; 陈明伟; 钱扬保; 张伟刚 |
| 刊名 | 无机材料学报
 |
| 出版日期 | 2012 |
| 卷号 | 27期号:12页码:1306 |
| ISSN号 | 1000-324X |
| 英文摘要 | A kind of BN/SiC open-cell ceramic foams were fabricated from complex co-polymeric precursors of polycarbosilane and tris(methylamino)borane B(NHCH3)(3) using a high-pressure pyrolysis foaming technique. The obtained foams exhibited cell sizes ranging from 1 mm to 5 mm with bulk densities varying from 0.44 g/cm(3) to 0.73 g/cm(3), depending on the proportion of the starting precursors. Studies on the microstructure and thermal property of the porous ceramics showed that the addition of BN into SiC could improve dramatically the oxidation resistance from 800 to 1100 degrees C. The compression strength of the composite foams was 5-10 times higher than that of pure SiC foam, which increased with increasing of BN content in the ceramic foams. Heat insulation performance of the ceramic foam fabricated from the starting precursors with a proportion of 1:1 in weight was analyzed by a device designed for insulation performance at high-temperature. When the temperature at the center point of hot surface of the foam was 1400 degrees C, the temperature at the center point of the back achieved only 280 degrees C. The heating history of the foam was simulated by finite- difference method, and the results showed that thermal conductivity of the composite foam was 4.0 W/(m.K), which was almost identical to the experimental result. |
| 语种 | 英语 |
| 源URL | [http://ir.ipe.ac.cn/handle/122111/37367]  |
| 专题 | 中国科学院过程工程研究所 |
| 作者单位 | 中国科学院过程工程研究所 |
| 推荐引用方式 GB/T 7714 | 沈志洵,戈敏,陈明伟,等. 前驱体热解氮化硼碳化硅复相泡沫陶瓷的抗氧化与高温隔热性能研究[J]. 无机材料学报,2012,27(12):1306. |
| APA | 沈志洵,戈敏,陈明伟,钱扬保,&张伟刚.(2012).前驱体热解氮化硼碳化硅复相泡沫陶瓷的抗氧化与高温隔热性能研究.无机材料学报,27(12),1306. |
| MLA | 沈志洵,et al."前驱体热解氮化硼碳化硅复相泡沫陶瓷的抗氧化与高温隔热性能研究".无机材料学报 27.12(2012):1306. |
入库方式： OAI收割
来源：过程工程研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。