Investigation of long-term thermal aging-induced dainage in oxide/oxide ceramic matrix composites
文献类型：期刊论文
| 作者 | Yang ZM(杨正茂)2 ; Yang JJ1
|
| 刊名 | JOURNAL OF THE EUROPEAN CERAMIC SOCIETY
 |
| 出版日期 | 2020-04-01 |
| 卷号 | 40期号:4页码:1549-1556 |
| ISSN号 | 0955-2219 |
| 关键词 | Ceramic matrix composites Thermal fatigue Thermal aging-induced damage Thermal aging Hierarchical porosity |
| DOI | 10.1016/j.jeurceramsoc.2019.10.052 |
| 通讯作者 | Yang, Zhengmao(zmyang@imech.ac.cn) |
| 英文摘要 | Long-term thermal aging is a typical factor affecting the thermo-mechanical fatigue life for hot-end components in the gas turbine. The present work focuses on the development of thermal aging-induced damage in 2-D woven oxide/oxide ceramic matrix composites from micro-mechanism and macroscopic mechanical performance. The porosity evolution and mechanical performance after long-term thermal aging were characterized through mercury intrusion measurements and uniaxial compressive tests, respectively. The results show that the decrease of micro-porosity directly reflects the irreversible evolution of material microstructure in the thermal aging process, and the decrease of compressive strength after aging is the macroscopic reflection of the microstructure variation. The porosity increment of matrix was thus used to characterize the thermal aging-induced damage, establishing a unique analysis model between the increment of micro-porosity under thermal aging and the corresponding degradation of material compressive strength. The experimental results are in good agreement with the established model. |
| 分类号 | 一类 |
| WOS关键词 | HIGH-TEMPERATURE EXPOSURE ; TENSILE-STRENGTH ; THERMOMECHANICAL DAMAGE ; MECHANICAL-BEHAVIOR ; ALUMINA FIBERS ; OXIDE FIBERS ; PERFORMANCE ; DEGRADATION ; EVOLUTION |
| 资助项目 | Strategic Priority Research Program of Chinese Academy of Sciences[XDA17030100] ; National Science Foundation of China[11572169] ; National Science Foundation of China[51775294] |
| WOS研究方向 | Materials Science |
| 语种 | 英语 |
| WOS记录号 | WOS:000514747500076 |
| 资助机构 | Strategic Priority Research Program of Chinese Academy of Sciences ; National Science Foundation of China |
| 其他责任者 | Yang, Zhengmao |
| 源URL | [http://dspace.imech.ac.cn/handle/311007/81562]  |
| 专题 | 空天飞行科技创新研究中心（筹） |
| 作者单位 | 1.Tsinghua Univ, Inst Aero Engines, Beijing, Peoples R China 2.Chinese Acad Sci, Inst Mech, Beijing, Peoples R China; |
| 推荐引用方式 GB/T 7714 | Yang ZM,Yang JJ. Investigation of long-term thermal aging-induced dainage in oxide/oxide ceramic matrix composites[J]. JOURNAL OF THE EUROPEAN CERAMIC SOCIETY,2020,40(4):1549-1556. |
| APA | 杨正茂,&Yang JJ.(2020).Investigation of long-term thermal aging-induced dainage in oxide/oxide ceramic matrix composites.JOURNAL OF THE EUROPEAN CERAMIC SOCIETY,40(4),1549-1556. |
| MLA | 杨正茂,et al."Investigation of long-term thermal aging-induced dainage in oxide/oxide ceramic matrix composites".JOURNAL OF THE EUROPEAN CERAMIC SOCIETY 40.4(2020):1549-1556. |
入库方式： OAI收割
来源：力学研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。