effectsofthecontinuouscoolingprocessconditionsonthecrystallizationandliberationcharacteristicsofanosoviteintibearingtitanomagnetitesmeltingslag
文献类型：期刊论文
| 作者 | Wang Zhen; Sun Haoyan; Zhu Qingshan |
| 刊名 | internationaljournalofmineralsmetallurgyandmaterials
 |
| 出版日期 | 2019 |
| 卷号 | 26期号:9页码:1120 |
| ISSN号 | 1674-4799 |
| 英文摘要 | This study involved the investigation of the effects of the continuous cooling process conditions on the crystallization and liberation characteristics of anosovite in Ti-bearing titanomagnetite smelting slag.The samples were heated until melting and then the temperature was held at 1650°C for nearly 0.5 h;subsequently,the samples were cooled at different cooling rates to different temperatures and water-quenched after being held for different times at these temperatures.Last,the obtained crystallized samples were used to analyze the crystallization and liberation characteristics.It was found that,during the continuous cooling process,anosovite particles were found to initially precipitate in the slag at a relatively high crystallization temperature,showing the characteristics of euhedral crystal.The precipitation and growth of anosovite grain is strong and the morphology of anosovite was basically not affected by the continuous cooling conditions.From the morphology perspective,the formed anosovite is an excellent Ti-rich phase to be selective separated.The formation of spinel and diopside is negative for the liberation and selective separation of the anosovite phase.The crystallization diagrams of TiO_2-MgO-CaO-SiO_2-Al_2O_3-FeO slag undergoing different continuous cooling processes were constructed to help to determine the optimal continuous cooling–quenching condition for selective separation of anosovite.Moreover,the addition of B_2O_3 can enlarge the range of the optimal continuous cooling– quenching conditions for selective separation of anosovite. |
| 语种 | 英语 |
| 源URL | [http://ir.ipe.ac.cn/handle/122111/39382]  |
| 专题 | 中国科学院过程工程研究所 |
| 作者单位 | 中国科学院过程工程研究所 |
| 推荐引用方式 GB/T 7714 | Wang Zhen,Sun Haoyan,Zhu Qingshan. effectsofthecontinuouscoolingprocessconditionsonthecrystallizationandliberationcharacteristicsofanosoviteintibearingtitanomagnetitesmeltingslag[J]. internationaljournalofmineralsmetallurgyandmaterials,2019,26(9):1120. |
| APA | Wang Zhen,Sun Haoyan,&Zhu Qingshan.(2019).effectsofthecontinuouscoolingprocessconditionsonthecrystallizationandliberationcharacteristicsofanosoviteintibearingtitanomagnetitesmeltingslag.internationaljournalofmineralsmetallurgyandmaterials,26(9),1120. |
| MLA | Wang Zhen,et al."effectsofthecontinuouscoolingprocessconditionsonthecrystallizationandliberationcharacteristicsofanosoviteintibearingtitanomagnetitesmeltingslag".internationaljournalofmineralsmetallurgyandmaterials 26.9(2019):1120. |
入库方式： OAI收割
来源：过程工程研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。