relationshipbetweenporestructureandhydrationactivityofcaofromcarbideslag
文献类型：期刊论文
| 作者 | Zhang Junqiang3; Zhang Shu2; Zhong Mei1; Wang Zhi3; Qian Guoyu3; Liu Junhao3; Gong Xuzhong3 |
| 刊名 | chinesejournalofchemicalengineering
 |
| 出版日期 | 2019 |
| 卷号 | 27期号:11页码:2771 |
| ISSN号 | 1004-9541 |
| 英文摘要 | CaO needs to show high activity to be used as Ca-sorbent and slagging agent. Hydration activity is an important characteristic to evaluate the activity of CaO. In this study, carbide slag from polyvinyl chloride (PVC) industry was utilized as precursor for preparing high activity CaO. The roles of crystallite grain, average pore diameter (APD) and volume fraction of pore < 200?nm in diameter (VF200) in hydration activity of CaO from carbide slag (CS-CaO) were respectively investigated. The hydrolysis kinetics model of CaO shows a three-dimensional spherically symmetric diffusion model (D4), which suggests that hydration activity was mainly associated with APD and VF200 of CS-CaO with limited correlation to the crystal size. Specifically, the hydration activity of CS-CaO is increased with increasing VF200, while decreased with increasing APD. Under the invariable calcination temperature, the core–shell structure formed by the addition of graphite or CaCO 3 to CS effectively inhibits the sintering of CS-CaO and improves VF200. Consequently, the hydration activity of CS-CaO increased from 22.79?°C·min ?1 to 27.19?°C·min ?1 and to 29.27?°C·min ?1 , with addition of 5% graphite or 5% CaCO 3 into carbide slag, respectively. |
| 语种 | 英语 |
| 源URL | [http://ir.ipe.ac.cn/handle/122111/40186]  |
| 专题 | 中国科学院过程工程研究所 |
| 作者单位 | 1.新疆大学 2.南京林业大学 3.中国科学院过程工程研究所 |
| 推荐引用方式 GB/T 7714 | Zhang Junqiang,Zhang Shu,Zhong Mei,et al. relationshipbetweenporestructureandhydrationactivityofcaofromcarbideslag[J]. chinesejournalofchemicalengineering,2019,27(11):2771. |
| APA | Zhang Junqiang.,Zhang Shu.,Zhong Mei.,Wang Zhi.,Qian Guoyu.,...&Gong Xuzhong.(2019).relationshipbetweenporestructureandhydrationactivityofcaofromcarbideslag.chinesejournalofchemicalengineering,27(11),2771. |
| MLA | Zhang Junqiang,et al."relationshipbetweenporestructureandhydrationactivityofcaofromcarbideslag".chinesejournalofchemicalengineering 27.11(2019):2771. |
入库方式： OAI收割
来源：过程工程研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。