Fracture surface morphology of brittle geomaterials influenced by loading rate and grain size
文献类型：期刊论文
| 作者 | Ju Minghe; Li Jianchun; Li Xiaofeng; Zhao Jian |
| 刊名 | INTERNATIONAL JOURNAL OF IMPACT ENGINEERING
 |
| 出版日期 | 2019 |
| 卷号 | 133页码:- |
| 关键词 | Crack deflection Crack penetration Surface roughness Dynamic loading Grain size |
| ISSN号 | 0734-743X |
| DOI | 10.1016/j.ijimpeng.2019.103363 |
| 英文摘要 | The fracture surface roughness of grain-based geomaterials is one of the significant factors reflecting the changes in certain physical and mechanical properties. In this paper, the transition of fracture surface roughness of brittle geomaterials with loading rate was investigated theoretically and experimentally. The notched semi-circular bending (NSCB) method was used to clarify the morphology transition mechanism integrating both the macro and micro-fracturing aspects of grain-based structures. Two measurement techniques, high-speed digital image correlation and a crack propagation gauge, were applied to acquire real-time crack locations and crack propagating velocities of NSCB samples under various dynamic loads. Macroscopic failure data were verified via our modified rate-dependent theoretical model for the prediction of crack deflection and penetration. Then the typical parameter, joint roughness coefficient (JRC), was used to characterise the micro-features of each fracture surface at different loading rates. This parameter is quantified in terms of the fractal dimension through our image processing method. In light of the comparisons of three scenarios under different degrees of dynamic loading, the JRC values linearly decrease with loading rate, which is attributed to the predominant failure pattern of microscopic grains changing from deflection to penetration. In addition, micro-grains in larger size on fracture surface roughness are more sensitive to the increase of loading rate, e.g. in rock, resulting in a greater decrease of fracture surface roughness with respect to that in cement with small micro-grains. However, if the crack propagation velocity exceeds the critical value that contributing to the micro-cracks branching, the declined fracture surface roughness will increase monotonically with the loading rate. The results help to predict the failure pattern of two-phase structures in both quasi-static and dynamic conditions as well allowing quantitative analysis of fracture surface morphology under dynamic load. |
| WOS研究方向 | Engineering ; Mechanics |
| 语种 | 英语 |
| WOS记录号 | WOS:000497248800020 |
| 源URL | [http://119.78.100.198/handle/2S6PX9GI/14834]  |
| 专题 | 岩土力学所知识全产出_期刊论文 国家重点实验室知识产出_期刊论文 |
| 作者单位 | 1.Monash Univ, Dept Civil Engn, Clayton, Vic 3800, Australia; 2.Southeast Univ, Inst Future Underground Space, Sch Civil Engn, Nanjing 211189, Jiangsu, Peoples R China; 3.Chinese Acad Sci, Inst Rock & Soil Mech, State Key Lab Geomech & Geotech Engn, Wuhan 430071, Hubei, Peoples R China |
| 推荐引用方式 GB/T 7714 | Ju Minghe,Li Jianchun,Li Xiaofeng,et al. Fracture surface morphology of brittle geomaterials influenced by loading rate and grain size[J]. INTERNATIONAL JOURNAL OF IMPACT ENGINEERING,2019,133:-. |
| APA | Ju Minghe,Li Jianchun,Li Xiaofeng,&Zhao Jian.(2019).Fracture surface morphology of brittle geomaterials influenced by loading rate and grain size.INTERNATIONAL JOURNAL OF IMPACT ENGINEERING,133,-. |
| MLA | Ju Minghe,et al."Fracture surface morphology of brittle geomaterials influenced by loading rate and grain size".INTERNATIONAL JOURNAL OF IMPACT ENGINEERING 133(2019):-. |
入库方式： OAI收割
来源：武汉岩土力学研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。