Corrosion Damage Behavior of Prestressed Rock Bolts under Aggressive Environment
文献类型：期刊论文
| 作者 | Zhu, Jiebing; Wang, Xiaowei; Li, Cong; Lu, Bo |
| 刊名 | KSCE JOURNAL OF CIVIL ENGINEERING
 |
| 出版日期 | 2019 |
| 卷号 | 23期号:7页码:3135-3145 |
| 关键词 | prestressed rock bolts corrosion damage aggressive environment electrochemical tests mechanical properties effective stress loss |
| ISSN号 | 1226-7988 |
| DOI | 10.1007/s12205-019-2420-0 |
| 英文摘要 | The corrosion of prestressed rock bolts (PRBs) has become a serious problem threatening the durability of prestressed anchorage structures during their service. This paper aims to investigate the corrosion damage mechanisms of the free lengths of PRBs subjected to an aggressive environment. During the experiment period, the corrosion behavior of the rock bolts was analyzed considering the influence of prestress under different pH (4, 5, 6, 7, and 8) amounts and several oxygen flow rates (OFR, 0 cm(3)/min, 40 cm(3)/min, 80 cm(3)/min, 120 cm(3)/min, and 160 cm(3)/min). Based on the electrochemical analysis, a corrosion rate (CR) development model of the PRBs related to the OFR was developed. The results indicated that the prestress had a great influence on the corrosion of the rock bolts. In the process of corrosion, the PRBs were in an activated state, and no passivation region was formed all the time. The corrosion degree of PRBs increased remarkably with an OFR ranging from 0 cm(3)/min to 80 cm(3)/min, and then it reached a threshold value. Additionally, the CR increment was insensitive to the OFR when the pH value was constant. It was observed that the loss rate of the ultimate elongation was larger than the other mechanical properties such as the ultimate tensile load loss rate and the elastic modulus. The effective stress loss of the PRBs under different conditions indicated that more attention is needed to be given to the specimens immersed in solutions with an OFR greater 40 cm(3)/min and pH lower than 6. |
| WOS研究方向 | Engineering |
| 语种 | 英语 |
| WOS记录号 | WOS:000474382800029 |
| 源URL | [http://119.78.100.198/handle/2S6PX9GI/14950]  |
| 专题 | 岩土力学所知识全产出_期刊论文 国家重点实验室知识产出_期刊论文 |
| 作者单位 | 1.Changjiang River Sci Res Inst, Minist Water Resources, Key Lab Geomech & Engn, Wuhan 430010, Hubei, Peoples R China; 2.Hohai Univ, Minist Educ Geomech & Embankment Engn, Key Lab, Nanjing 210098, Jiangsu, Peoples R China |
| 推荐引用方式 GB/T 7714 | Zhu, Jiebing,Wang, Xiaowei,Li, Cong,et al. Corrosion Damage Behavior of Prestressed Rock Bolts under Aggressive Environment[J]. KSCE JOURNAL OF CIVIL ENGINEERING,2019,23(7):3135-3145. |
| APA | Zhu, Jiebing,Wang, Xiaowei,Li, Cong,&Lu, Bo.(2019).Corrosion Damage Behavior of Prestressed Rock Bolts under Aggressive Environment.KSCE JOURNAL OF CIVIL ENGINEERING,23(7),3135-3145. |
| MLA | Zhu, Jiebing,et al."Corrosion Damage Behavior of Prestressed Rock Bolts under Aggressive Environment".KSCE JOURNAL OF CIVIL ENGINEERING 23.7(2019):3135-3145. |
入库方式： OAI收割
来源：武汉岩土力学研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。