Investigation on the microstructure and mechanical properties of autogenous laser welding joint of ITER BTCC case lid
文献类型：期刊论文
| 作者 | Dai Wen-Hua1,2; Song Yun-Tao1,2; Xin Ji-Jun1,2; Chao, Fang1; Jing, Wei1 ; Wu Jie-Feng1
|
| 刊名 | FUSION ENGINEERING AND DESIGN
 |
| 出版日期 | 2020-07-01 |
| 卷号 | 156 |
| ISSN号 | 0920-3796 |
| 关键词 | 316LN Laser welding Microstructure Mechanical properties |
| DOI | 10.1016/j.fusengdes.2020.111607 |
| 通讯作者 | Jing, Wei(jingw@ipp.ac.cn) |
| 英文摘要 | The 316LN stainless steel with a thickness of 21 mm was welded by autogenous laser welding from both sides with an YLS-20000 fiber laser welding system. The microstructure of the welding joint was characterized by optical microscope. The tensile and bending tests were performed at room temperature and impact testing was conducted at 4.2 K. The results show that the thickness of the remelting region decreases with the increase of welding speed. The microstructure of the weld zone was single austenite phase. The tensile strength of the welded joint is 623 MPa at room temperature, equal to that of the base material (624 MPa). The fracture was located in the base metal. The bending test of the welding joint shows that no micro crack could be found on the surface of the samples after bending to 180 degrees, which indicates that the welded joint has good bending strength and plasticity. The average impact absorption energy of the welding area and heat affected zone at 4.2 K is 173 +/- 10 J and 241 +/- 8 J, respectively. The fracture surface shows a typical ductile fracture mode featured with fine equiaxed dimples and tearing ridges. All the test results meet the ITER design requirement. |
| WOS关键词 | TOUGHNESS BEHAVIOR ; METAL ; STEEL ; STRENGTH |
| 资助项目 | National Natural Science Foundation of China[51525703] ; ITER IO magnet division |
| WOS研究方向 | Nuclear Science & Technology |
| 语种 | 英语 |
| 出版者 | ELSEVIER SCIENCE SA |
| WOS记录号 | WOS:000547855400010 |
| 资助机构 | National Natural Science Foundation of China ; ITER IO magnet division |
| 源URL | [http://ir.hfcas.ac.cn:8080/handle/334002/71141]  |
| 专题 | 中国科学院合肥物质科学研究院 |
| 通讯作者 | Jing, Wei |
| 作者单位 | 1.Chinese Acad Sci, Inst Plasma Phys, Hefei 230031, Peoples R China 2.Univ Sci & Technol China, Hefei 230026, Peoples R China |
| 推荐引用方式 GB/T 7714 | Dai Wen-Hua,Song Yun-Tao,Xin Ji-Jun,et al. Investigation on the microstructure and mechanical properties of autogenous laser welding joint of ITER BTCC case lid[J]. FUSION ENGINEERING AND DESIGN,2020,156. |
| APA | Dai Wen-Hua,Song Yun-Tao,Xin Ji-Jun,Chao, Fang,Jing, Wei,&Wu Jie-Feng.(2020).Investigation on the microstructure and mechanical properties of autogenous laser welding joint of ITER BTCC case lid.FUSION ENGINEERING AND DESIGN,156. |
| MLA | Dai Wen-Hua,et al."Investigation on the microstructure and mechanical properties of autogenous laser welding joint of ITER BTCC case lid".FUSION ENGINEERING AND DESIGN 156(2020). |
入库方式： OAI收割
来源：合肥物质科学研究院
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。