Optical properties of transparent ZnSe0.9S0.1 mixed crystal ceramics prepared by hot isostatic pressing
文献类型：期刊论文
| 作者 | Lu, H; Liu, P; Tao, XH; Wang, J; Jiang, ZS; Zhang, J; Xu, XD; Tang, DY |
| 刊名 | OPTICAL MATERIALS
 |
| 出版日期 | 2020-10-01 |
| ISSN号 | 0925-3467 |
| DOI | 10.1016/j.optmat.2020.110214 |
| 文献子类 | Article |
| 英文摘要 | Mid-infrared ZnSe0.9S0.1 transparent mixed crystal ceramics were successfully fabricated by hot pressing (HP) in combination with post hot isostatic pressing (HIP). The phase structure of the as-fabricated mixed ceramics was found to be composed of cubic sphalerite, and the existence of any secondary phase was not detected. It was noticed that after post HIP treatment, the grain size increased greatly, and many closed pores in the samples disappeared. The specimens HP sintered at 1000 degrees C under 60 MPa and post HIP treated at 1300 degrees C under 196 MPa in the Ar atmosphere for six hours had the best transmission of 62.3% at 14 mu m. |
| WOS关键词 | ZINC SELENIDE ; ZNS CERAMICS ; SULFIDE ; PHOTOLUMINESCENCE |
| WOS研究方向 | Materials Science ; Optics |
| 语种 | 英语 |
| 出版者 | ELSEVIER |
| 源URL | [http://ir.sic.ac.cn/handle/331005/27705]  |
| 专题 | 中国科学院上海硅酸盐研究所 |
| 推荐引用方式 GB/T 7714 | Lu, H,Liu, P,Tao, XH,et al. Optical properties of transparent ZnSe0.9S0.1 mixed crystal ceramics prepared by hot isostatic pressing[J]. OPTICAL MATERIALS,2020. |
| APA | Lu, H.,Liu, P.,Tao, XH.,Wang, J.,Jiang, ZS.,...&Tang, DY.(2020).Optical properties of transparent ZnSe0.9S0.1 mixed crystal ceramics prepared by hot isostatic pressing.OPTICAL MATERIALS. |
| MLA | Lu, H,et al."Optical properties of transparent ZnSe0.9S0.1 mixed crystal ceramics prepared by hot isostatic pressing".OPTICAL MATERIALS (2020). |
入库方式： OAI收割
来源：上海硅酸盐研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。