Effect of starting materials and sintering temperature on microstructure and optical properties of Y2O3:Yb(3+)5 at% transparent ceramics
文献类型：期刊论文
| 作者 | Yavetskiy, RP; Balabanov, AE; Parkhomenko, SV; Kryzhanovska, OS; Doroshenko, AG; Mateychenko, PV; Tolmachev, AV; Li, J; Jiang, N; Gheorghe, L |
| 刊名 | JOURNAL OF ADVANCED CERAMICS
 |
| 出版日期 | 2020-09-24 |
| ISSN号 | 2226-4108 |
| DOI | 10.1007/s40145-020-0416-3 |
| 文献子类 | Article; Early Access |
| 英文摘要 | Y2O3:Yb(3+)5 at% ceramics have been synthesized by the reactive sintering method using different commercial yttria powders (Alfa-Micro, Alfa-Nano, and ITO-V) as raw materials. It has been shown that all Y(2)O(3)starting powders consist from agglomerates up to 5-7 mu m in size which are formed from 25-60 nm primary particles. High-energy ball milling allows to significantly decreasing the median particle sizeD(50)below 500 nm regardless of the commercial powders used. Sintering experiments indicate that powder mixtures fabricated from Alfa-Nano yttria powders have the highest sintering activity, while (Y0.86La0.09Yb0.05)(2)O(3)ceramics sintered at 1750 degrees C for 10 h are characterized by the highest transmittance of about 45%. Y2O3:Yb(3+)ceramics have been obtained by the reactive sintering at 1750-1825 degrees C using Alfa-Nano Y(2)O(3)powders and La2O3+ZrO(2)as a complex sintering aid. The effects of the sintering temperature on densification processes, microstructure, and optical properties of Y2O3:Yb(3)(+)5 at% ceramics have been studied. It has been shown that Zr(4)(+)ions decrease the grain growth of Y2O3:Yb(3+)ceramics for sintering temperatures 1750-1775 degrees C. Further increasing the sintering temperature was accompanied by a sharp increase of the average grain size of ceramics referred to changes of structure and chemical composition of grain boundaries, as well as their mobility. It has been determined that the optimal sintering temperature to produce high-dense yttria ceramics with transmittance of 79%-83% and average grain size of 8 mu m is 1800 degrees C. Finally, laser emission at similar to 1030.7 nm with a slope efficiency of 10% was obtained with the most transparent Y2O3:Yb(3+)5 at% ceramics sintered. |
| WOS关键词 | CONTINUOUS-WAVE ; DOPED Y2O3 ; FABRICATION ; LUMINESCENCE ; LA2O3 ; ZRO2 |
| WOS研究方向 | Materials Science |
| 语种 | 英语 |
| 出版者 | SPRINGER |
| 源URL | [http://ir.sic.ac.cn/handle/331005/27739]  |
| 专题 | 中国科学院上海硅酸盐研究所 |
| 推荐引用方式 GB/T 7714 | Yavetskiy, RP,Balabanov, AE,Parkhomenko, SV,et al. Effect of starting materials and sintering temperature on microstructure and optical properties of Y2O3:Yb(3+)5 at% transparent ceramics[J]. JOURNAL OF ADVANCED CERAMICS,2020. |
| APA | Yavetskiy, RP.,Balabanov, AE.,Parkhomenko, SV.,Kryzhanovska, OS.,Doroshenko, AG.,...&Enculescu, M.(2020).Effect of starting materials and sintering temperature on microstructure and optical properties of Y2O3:Yb(3+)5 at% transparent ceramics.JOURNAL OF ADVANCED CERAMICS. |
| MLA | Yavetskiy, RP,et al."Effect of starting materials and sintering temperature on microstructure and optical properties of Y2O3:Yb(3+)5 at% transparent ceramics".JOURNAL OF ADVANCED CERAMICS (2020). |
入库方式： OAI收割
来源：上海硅酸盐研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。