Investigation on low-temperature reactive viscous flow sintering behavior of lanthanum-borate glass-ceramic with BaTi4O9 ceramic filler
文献类型:期刊论文
作者 | Lu, XZ; Lin, HX |
刊名 | JOURNAL OF THE EUROPEAN CERAMIC SOCIETY |
出版日期 | 2020-09-01 |
期号 | 12页码:4035 |
ISSN号 | 0955-2219 |
DOI | 10.1016/j.jeurceramsoc.2020.05.025 |
文献子类 | Article |
英文摘要 | In this paper, the sintering behavior of the lanthanum-borate (B2O3-La2O3-MgO-TiO2,BLMT) glass-ceramic with BaTi4O9 filler composite was investigated in terms of the wetting behavior, interfacial reaction, sinter-shrinkage process, sintering activation energy, as well as phase and microstructure evolution with change in filler contents and sintering temperature. Our research suggested that the glass is unable to wet the filler material within a temperature up to 1000 degrees C, indicating that the densification process of composites is dominated by viscous flow of glass matrix. The increase in filler content that performs as a rigid particle in composite causes the rise in the sinter-shrinkage-onset and -end temperature, thereby proving that the viscous-flow densification of the composites with x <= 30 wt% filler content is accomplished before the crystallization of BLMT glass, whereas the composites with x >= 40 wt% cannot. After densification, a chemical reaction that almost synchronizes with the glass crystallization occurred between glass and ceramic, which not only imposes significant influence on the crystallization behavior, but eradicates the closed pore formed by the viscous flow and the induced crystallization porosity. The densification process of the BaTi4O9 filler-BLMT glass composite was referred to as two-stage reactive assisted viscous flow sintering process which consists of viscous flow of glass, of the crystallization process of glass, and/or of the chemical reaction between glass and filler. |
WOS关键词 | MICROWAVE DIELECTRIC-PROPERTIES ; PHASE EVOLUTION ; CRYSTALLIZATION ; DENSIFICATION ; KINETICS ; VISCOSITY ; POWDERS |
WOS研究方向 | Materials Science |
语种 | 英语 |
出版者 | ELSEVIER SCI LTD |
源URL | [http://ir.sic.ac.cn/handle/331005/27794] |
专题 | 中国科学院上海硅酸盐研究所 |
推荐引用方式 GB/T 7714 | Lu, XZ,Lin, HX. Investigation on low-temperature reactive viscous flow sintering behavior of lanthanum-borate glass-ceramic with BaTi4O9 ceramic filler[J]. JOURNAL OF THE EUROPEAN CERAMIC SOCIETY,2020(12):4035. |
APA | Lu, XZ,&Lin, HX.(2020).Investigation on low-temperature reactive viscous flow sintering behavior of lanthanum-borate glass-ceramic with BaTi4O9 ceramic filler.JOURNAL OF THE EUROPEAN CERAMIC SOCIETY(12),4035. |
MLA | Lu, XZ,et al."Investigation on low-temperature reactive viscous flow sintering behavior of lanthanum-borate glass-ceramic with BaTi4O9 ceramic filler".JOURNAL OF THE EUROPEAN CERAMIC SOCIETY .12(2020):4035. |
入库方式: OAI收割
来源:上海硅酸盐研究所
浏览0
下载0
收藏0
其他版本
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。