Biocompatibility and bone regeneration of PEO/Mg-Al LDH-coated pure Mg: an in vitro and in vivo study
文献类型：期刊论文
| 作者 | Wang, J; Peng, F; Wu, XL; Wang, DH; Zheng, A; Cao, LY; Yu, CH; Liu, XY; Jiang, XQ |
| 刊名 | SCIENCE CHINA-MATERIALS
 |
| 出版日期 | 2020-08-11 |
| ISSN号 | 2095-8226 |
| DOI | 10.1007/s40843-020-1392-5 |
| 文献子类 | Article; Early Access |
| 英文摘要 | Forming a stable anti-corrosion surface layer on magnesium (Mg) and its alloys has become a major challenge in developing a desirable degradable medical implant in bone. In this study, a porous MgO layer was first formed on Mg by plasma electrolytic oxidation (PEO), and then a Mg-Al layered double hydroxide (LDH) layer was prepared to seal the porous structure of the PEO layer (LDH-2h and LDH-12h)viahydrothermal treatment. The bilayer structure composite coating, which can effectively resist the penetration of surrounding media, is similar to plain Chinese tiles. Thein vitroresults revealed that compared with other coatings, the LDH-12h composite coating can reduce the release of Mg ions and induce a milder change in pH when immersed in phosphate-buffered saline (PBS).In vitrorat bone marrow stem cell (rBMSC) culture suggested that the LDH-12h composite coating is favorable for cell activity, proliferation and could improve the osteogenic activity of rBMSCs. A subcutaneous implantation test revealed that the as-prepared sample showed enhanced corrosion resistance and histocompatibilityin vivo, especially in the LDH-12h group. Moreover, LDH-12h had the lowest rate of degradation and the closest combination with the new bone after being inserted into a rat femur for 12 weeks with no major organ dysfunction. In summary, the asprepared PEO/Mg-Al LDH composite coating is able to improve the corrosion resistance and biocompatibility of Mg and to enhance osteogenic activityin vivo, suggesting its promising prospects for orthopedic applications. |
| WOS关键词 | MICRO-ARC OXIDATION ; MAGNESIUM ALLOY ; CORROSION-RESISTANCE ; ELECTROLYTIC OXIDATION ; SURFACE MODIFICATION ; ORTHOPEDIC IMPLANTS ; CA ALLOYS ; DEGRADATION ; CYTOCOMPATIBILITY ; BEHAVIOR |
| WOS研究方向 | Materials Science |
| 语种 | 英语 |
| 出版者 | SCIENCE PRESS |
| 源URL | [http://ir.sic.ac.cn/handle/331005/27841]  |
| 专题 | 中国科学院上海硅酸盐研究所 |
| 推荐引用方式 GB/T 7714 | Wang, J,Peng, F,Wu, XL,et al. Biocompatibility and bone regeneration of PEO/Mg-Al LDH-coated pure Mg: an in vitro and in vivo study[J]. SCIENCE CHINA-MATERIALS,2020. |
| APA | Wang, J.,Peng, F.,Wu, XL.,Wang, DH.,Zheng, A.,...&Jiang, XQ.(2020).Biocompatibility and bone regeneration of PEO/Mg-Al LDH-coated pure Mg: an in vitro and in vivo study.SCIENCE CHINA-MATERIALS. |
| MLA | Wang, J,et al."Biocompatibility and bone regeneration of PEO/Mg-Al LDH-coated pure Mg: an in vitro and in vivo study".SCIENCE CHINA-MATERIALS (2020). |
入库方式： OAI收割
来源：上海硅酸盐研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。