The electrical and optical properties of Nb-doping PLZT (9/65/35) transparent ceramics
文献类型：期刊论文
| 作者 | Xu, ZW; Zeng, X; Cao, ZD; Ling, L; Qiu, PS; He, XY |
| 刊名 | JOURNAL OF ELECTROCERAMICS
 |
| 出版日期 | 2020-06-01 |
| 期号 | 2020-03-04页码:215 |
| ISSN号 | 1385-3449 |
| DOI | 10.1007/s10832-020-00212-9 |
| 文献子类 | Article |
| 英文摘要 | In the past few decades, transparent electro-optical ceramics PLZT (9/65/35) (Pb0.91La0.09(Zr0.65Ti0.35)(0.9775)O-3) with special properties, particularly high transmittance in visible light, have gained much attention. However, restricted by the large ferroelectric hysteresis, the prospect is not optimistic. In this article, Pb0.91La0.09(Zr0.65Ti0.35)(0.9775-5x/4)NbxO3 (abbreviated as PLZTN) transparent ceramics with varying Nb content (x = 0.000, 0.005, 0.010, 0.015) were fabricated by hot press sintering process under oxygen atmosphere. Electrical and optical properties were systematically studied. The temperature dependence of the dielectric constant showed a diffuse phase transition indicated typical relaxor behaviour. Moreover, the temperature at maximum dielectric constant (T-m) are near about 63 degrees C, almost unchanged. Comparing with undoped samples, the PLZTN with x = 0.010 Nb doping shows a dramatic reduction of 162.5% in ferroelectric hysteresis, with only a slight decrease in the maximum polarization from 30.04 mu C/cm(2) to 28.53 mu C/cm(2). The quadratic electro optic coefficient experienced 54.8% reduction but still satisfy the application requirements. In terms of transmittance, the PLZTN samples kept a high value of transmittance (about 64%) along with increasing Nb content. Hence, the conclusion can be drawn that Nb doping in PLZT (9/65/35) is a novel strategy to reduce the ferroelectric hysteresis. |
| WOS关键词 | B-SITE ; A-SITE ; PZT ; MICROSTRUCTURE ; DY |
| WOS研究方向 | Materials Science |
| 语种 | 英语 |
| 出版者 | SPRINGER |
| 源URL | [http://ir.sic.ac.cn/handle/331005/28044]  |
| 专题 | 中国科学院上海硅酸盐研究所 |
| 推荐引用方式 GB/T 7714 | Xu, ZW,Zeng, X,Cao, ZD,et al. The electrical and optical properties of Nb-doping PLZT (9/65/35) transparent ceramics[J]. JOURNAL OF ELECTROCERAMICS,2020(2020-03-04):215. |
| APA | Xu, ZW,Zeng, X,Cao, ZD,Ling, L,Qiu, PS,&He, XY.(2020).The electrical and optical properties of Nb-doping PLZT (9/65/35) transparent ceramics.JOURNAL OF ELECTROCERAMICS(2020-03-04),215. |
| MLA | Xu, ZW,et al."The electrical and optical properties of Nb-doping PLZT (9/65/35) transparent ceramics".JOURNAL OF ELECTROCERAMICS .2020-03-04(2020):215. |
入库方式： OAI收割
来源：上海硅酸盐研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。