Novel (Tb0.99Ce0.01)(3)Ga5O12 magneto-optical ceramics for Faraday isolators
文献类型：期刊论文
| 作者 | Li, XY; Liu, Q; Liu, X; Chen, XP; Wu, LX; Xie, TF; Shi, Y; Chen, HH; Li, J |
| 刊名 | SCRIPTA MATERIALIA
 |
| 出版日期 | 2020-03-01 |
| 页码 | 137 |
| ISSN号 | 1359-6462 |
| DOI | 10.1016/j.scriptamat.2019.10.023 |
| 文献子类 | Article |
| 英文摘要 | (Tb0.99Ce0.01)(3)Ga5O12 powders were synthesized by calcining the co-precipitated precursor at 1150 degrees C. The powders showed low-agglomeration and high sinterability, so that the powders compact could be sintered to be transparent by a two-step sintering method. By using the best synthesis condition of air pre-sintered at 1525 degrees C for 3 h and hot isostatic pressed at 1500 degrees C for 3 h under 150 MPa, (Tb0.99Ce0.01)(3)Ga5O12 transparent ceramics with the in -line transmittance of 81.7% at 1064 nm were successfully prepared. The Verdet constant of the (Tb0.99Ce0.01)(3)Ga5O12 ceramics at 633 nm was about -143.4 +/- 3.2 rad T-1 m(-1), which was about 7% higher than that of the Tb3Ga5O12 crystals (-134 rad T-1 m(-1)). (C) 2019 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved. |
| WOS关键词 | TERBIUM GALLIUM GARNET ; INDUCED DEPOLARIZATION ; WAVELENGTH DEPENDENCE ; VERDET CONSTANT ; FABRICATION ; LASER ; TB3GA5O12 ; SELF ; ALUMINUM ; POWDERS |
| WOS研究方向 | Science & Technology - Other Topics ; Materials Science ; Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| 出版者 | PERGAMON-ELSEVIER SCIENCE LTD |
| 源URL | [http://ir.sic.ac.cn/handle/331005/28277]  |
| 专题 | 中国科学院上海硅酸盐研究所 |
| 推荐引用方式 GB/T 7714 | Li, XY,Liu, Q,Liu, X,et al. Novel (Tb0.99Ce0.01)(3)Ga5O12 magneto-optical ceramics for Faraday isolators[J]. SCRIPTA MATERIALIA,2020:137. |
| APA | Li, XY.,Liu, Q.,Liu, X.,Chen, XP.,Wu, LX.,...&Li, J.(2020).Novel (Tb0.99Ce0.01)(3)Ga5O12 magneto-optical ceramics for Faraday isolators.SCRIPTA MATERIALIA,137. |
| MLA | Li, XY,et al."Novel (Tb0.99Ce0.01)(3)Ga5O12 magneto-optical ceramics for Faraday isolators".SCRIPTA MATERIALIA (2020):137. |
入库方式： OAI收割
来源：上海硅酸盐研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。