Leakage behavior of toxic substances of naphthalene sulfonate-formaldehyde condensation from cement based materials
文献类型：期刊论文
| 作者 | Gu, LN; Li, HX; Yang, XJ; Dong, BQ; Wen, ZY |
| 刊名 | JOURNAL OF ENVIRONMENTAL MANAGEMENT
 |
| 出版日期 | 2020-02-01 |
| ISSN号 | 0301-4797 |
| DOI | 10.1016/j.jenvman.2019.109934 |
| 文献子类 | Article |
| 英文摘要 | Naphthalene sulfonate-formaldehyde condensatation (NSF) is the main component of the naphthalene based water reducers for cement based materials, as well as an organic substance with potential toxicity. However it is still uncertain whether it can leak from the cement based materials. In this work, the leakage ratio and adsorption behavior of NSF from various cement based materials such as the different water/cement (w/c) ratio, NSF content, types of cementitious materials as well as at different hydration time were evaluated. The product components of the cement based materials cured for different times were also quantified to explore the mechanisms which are responsible for the leakage and adsorption behaviors. The results indicate that more NSF, lower w/c ratio and less mineral admixture decrease the NSF leakage ratio. The leakage ratio of NSF from cement paste mixed 0.3% NSF is up to 50.8% at 0.5 h, and it decreases to 31.0% at 28 d. The leakage ratio of NSF from cement paste decreases as the hydration time prolongs. The lower leakage ratio corresponds to the higher adsorption capacity. Less adsorption capacity and thinner adsorption film imply that lower temperature and mineral admixture decrease the NSF adsorption behavior. When 0.3% NSF is added into the cement paste, the adsorption amount and NSF layer thickness are 5.53 mg/g and 0.98 nm, 5.87 mg/g and 4.7 nm at 0.5 h and 28 d respectively. The result demonstrates that the adsorption behavior of NSF in cement significantly increases at the initial several hours and gradually stabilizes after the first day. The X-ray powder diffractometer (XRD) results show thatthe contents of tricalcium silicate (C3S) and dicalcium silicate (C2S) continuously decline and the amorphous phases and ettringite (AFt) increase rapidly in the early stage. NSF adsorption and leakage behaviors are closely related to the hydration process of cement. These results indicate that NSF can definitely leak from the cement based materials and thus the NSF potential environmental pollution cannot be ignored. At least, it should be restricted or cautious to produce the water tower and pipe concrete structure with it. These results will sever as a theoretically reference for the pollution control as well as better application of NSF in cement-based materials. |
| WOS关键词 | HYDRATION ; SUPERPLASTICIZER ; MICROSTRUCTURE ; STRENGTH ; PERFORMANCE ; ADSORPTION ; POLLUTANTS ; CONCRETE ; MORTAR ; POWDER |
| WOS研究方向 | Environmental Sciences & Ecology |
| 语种 | 英语 |
| 出版者 | ACADEMIC PRESS LTD- ELSEVIER SCIENCE LTD |
| 源URL | [http://ir.sic.ac.cn/handle/331005/28330]  |
| 专题 | 中国科学院上海硅酸盐研究所 |
| 推荐引用方式 GB/T 7714 | Gu, LN,Li, HX,Yang, XJ,et al. Leakage behavior of toxic substances of naphthalene sulfonate-formaldehyde condensation from cement based materials[J]. JOURNAL OF ENVIRONMENTAL MANAGEMENT,2020. |
| APA | Gu, LN,Li, HX,Yang, XJ,Dong, BQ,&Wen, ZY.(2020).Leakage behavior of toxic substances of naphthalene sulfonate-formaldehyde condensation from cement based materials.JOURNAL OF ENVIRONMENTAL MANAGEMENT. |
| MLA | Gu, LN,et al."Leakage behavior of toxic substances of naphthalene sulfonate-formaldehyde condensation from cement based materials".JOURNAL OF ENVIRONMENTAL MANAGEMENT (2020). |
入库方式： OAI收割
来源：上海硅酸盐研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。