Influences of the Sc3+ content on the microstructure and optical properties of 10 at.% Yb:Y3ScxAl5-xO12 laser ceramics
文献类型：期刊论文
| 作者 | Feng, YG; Toci, G; Pirri, A; Patrizi, B; Chen, XP; Wei, JB; Pan, HM; Zhang, X; Li, XY; Vannini, M |
| 刊名 | JOURNAL OF ALLOYS AND COMPOUNDS
 |
| 出版日期 | 2020-01-30 |
| ISSN号 | 0925-8388 |
| DOI | 10.1016/j.jallcom.2019.152637 |
| 文献子类 | Article |
| 英文摘要 | 10 at.% Yb:Y3ScxAl5-xO12 (x = 0.25, 0.5, 1.0 and 1.5) transparent ceramics have been successfully fabricated by the solid state reaction method combined with vacuum sintering, whose transmittances reach 80% at 1100 nm with thickness of 3.0 mm. The full width at half maximum (FWHM) of the emission peaks located at about 1030 nm increases for increasing the Sc3+ content, and a maximum FWHM of 14.53 nm is obtained for 10 at.% Yb:Y3Sc1.5Al3.5O12 ceramics, which is 1.4 times larger than that of the 10 at.% Yb:Y3Al5O12 (Yb:YAG) ceramics. Finally, the laser performance of the 10 at.% Yb:Y3Sc1.5Al3.5O12 ceramics was tested and compared with that of a standard 10 at.% Yb:YAG sample. In quasi continuous wave (QCW) regime, a maximum laser output power of 10.8 W was obtained with the slope efficiency of 66.4%. The tuning range significantly broadens in the case of the Yb:YSAG sample, reaching a width of 86.2 nm. (C) 2019 Elsevier B.V. All rights reserved. |
| WOS关键词 | MODE-LOCKING ; FABRICATION ; GENERATION ; EMISSION ; Y3AL5O12 |
| WOS研究方向 | Chemistry ; Materials Science ; Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| 出版者 | ELSEVIER SCIENCE SA |
| 源URL | [http://ir.sic.ac.cn/handle/331005/28359]  |
| 专题 | 中国科学院上海硅酸盐研究所 |
| 推荐引用方式 GB/T 7714 | Feng, YG,Toci, G,Pirri, A,et al. Influences of the Sc3+ content on the microstructure and optical properties of 10 at.% Yb:Y3ScxAl5-xO12 laser ceramics[J]. JOURNAL OF ALLOYS AND COMPOUNDS,2020. |
| APA | Feng, YG.,Toci, G.,Pirri, A.,Patrizi, B.,Chen, XP.,...&Li, J.(2020).Influences of the Sc3+ content on the microstructure and optical properties of 10 at.% Yb:Y3ScxAl5-xO12 laser ceramics.JOURNAL OF ALLOYS AND COMPOUNDS. |
| MLA | Feng, YG,et al."Influences of the Sc3+ content on the microstructure and optical properties of 10 at.% Yb:Y3ScxAl5-xO12 laser ceramics".JOURNAL OF ALLOYS AND COMPOUNDS (2020). |
入库方式： OAI收割
来源：上海硅酸盐研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。