Microstructure and oxidation behaviour of Pt modified NiCrAlYSi coating on a Ni-based single crystal superalloy
文献类型：期刊论文
| 作者 | Sun, J.; Xiao, H.; Li, W.; Liu, S. B.; Fu, L. B.; Jiang, S. M. |
| 刊名 | SURFACE & COATINGS TECHNOLOGY
 |
| 出版日期 | 2020-10-15 |
| 卷号 | 399 |
| DOI | 10.1016/j.surfcoat.2020.126164 |
| 英文摘要 | In this study, the N + NiCrAlYSi coating and NiCrAlYSi + N coating were produced onto the Ni-based single crystal superalloy by using the arc ion plating (AIP) and electroplating. For the N + NiCrAlYSi coating, the N mainly distributed in substrate and the bottom of coating, while the N primarily located at the outer part of NiCrAlYSi + N coating. After isothermal oxidation at 1100 degrees C, the weight gains for the NiCrAlYSi coating, N + NiCrAlYSi coating and NiCrAlYSi + N coating were 1.81 mg/cm(2), 1.68 mg/cm(2) and 1.37 mg/cm(2), respectively. The parabolic rate constant of the NiCrAlYSi +N coating was 6.2 x 10(-3) mg(2) cm(-4) h(-1), which was the smallest among three kinds of coatings. The mass of spalled oxides for the NiCrAlYSi coating, N + NiCrAlYSi coating and NiCrAlYSi + N coating were 2.07 mg/cm(2), 0.937 mg/cm(2) and 0.801 mg/cm(2) after cyclic oxidation at 1150 degrees C. So, the addition of N in the NiCrA1YSi coating can significantly improve the adhesion of alumina scale. The oxidation WA results indicated that the NiCrAlYSi + N coating showed the best oxidation resistance. Some Pt-rich particles were observed on the surface of the NiCrAlYSi + N coating after 1 cycle at 1150 degrees C. The enrichment of N on the outer part of NiCrAlYSi + N coating can increase the out diffusion flux of Al and promote the fast formation of pure Al2O3 at the early stage of oxidation. |
| WOS记录号 | WOS:000563807700052 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/82439]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | Sun, J.,Xiao, H.,Li, W.,et al. Microstructure and oxidation behaviour of Pt modified NiCrAlYSi coating on a Ni-based single crystal superalloy[J]. SURFACE & COATINGS TECHNOLOGY,2020,399. |
| APA | Sun, J.,Xiao, H.,Li, W.,Liu, S. B.,Fu, L. B.,&Jiang, S. M..(2020).Microstructure and oxidation behaviour of Pt modified NiCrAlYSi coating on a Ni-based single crystal superalloy.SURFACE & COATINGS TECHNOLOGY,399. |
| MLA | Sun, J.,et al."Microstructure and oxidation behaviour of Pt modified NiCrAlYSi coating on a Ni-based single crystal superalloy".SURFACE & COATINGS TECHNOLOGY 399(2020). |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。