Effect of post-irradiation annealing on microstructure and corrosion of proton-irradiated 308L stainless steel weld metal
文献类型：期刊论文
| 作者 | Lin, Xiaodong; Han, En-Hou; Peng, Qunjia; Ke, Wei; Jiao, Zhijie |
| 刊名 | CORROSION SCIENCE
 |
| 出版日期 | 2020-10-01 |
| 卷号 | 175 |
| DOI | 10.1016/j.corsci.2020.108887 |
| 英文摘要 | The effect of post-irradiation annealing (PIA) at 550 degrees C for 1 h on microstructure and corrosion of proton-irradiated 308L stainless steel weld metal was investigated. After PIA, growth of voids and Frank loops in austenite occurred, whereas Ni/Si-rich clusters in austenite, spinodal decomposition and G-phase in delta-ferrite, and segregation at grain boundary were removed. Corrosion experiments showed that the inner oxide thickness of austenite was increased by PIA, while the oxide scale on delta-ferrite was unaffected. In addition, localized corrosion was not observed along the grain boundary and carbide-free phase boundary, while it still remained along the carbide-containing phase boundary. |
| WOS记录号 | WOS:000582435000002 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/82463]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | Lin, Xiaodong,Han, En-Hou,Peng, Qunjia,et al. Effect of post-irradiation annealing on microstructure and corrosion of proton-irradiated 308L stainless steel weld metal[J]. CORROSION SCIENCE,2020,175. |
| APA | Lin, Xiaodong,Han, En-Hou,Peng, Qunjia,Ke, Wei,&Jiao, Zhijie.(2020).Effect of post-irradiation annealing on microstructure and corrosion of proton-irradiated 308L stainless steel weld metal.CORROSION SCIENCE,175. |
| MLA | Lin, Xiaodong,et al."Effect of post-irradiation annealing on microstructure and corrosion of proton-irradiated 308L stainless steel weld metal".CORROSION SCIENCE 175(2020). |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。