Magnesium carbonate precipitation under the influence of polyacrylamide
文献类型：期刊论文
| 作者 | Li, Quan ; Ye, Xiushen; Wu, Zhijian; Guo, Min
|
| 刊名 | POWDER TECHNOLOGY
 |
| 出版日期 | 2010 |
| 卷号 | 200期号:1-2页码:46-51 |
| ISSN号 | 0032-5910 |
| 英文摘要 | The precipitation of magnesium carbonate by the reaction of MgCl(2) with Na(2)CO(3), under the influence of polyacrylamide (PAM) was studied. Factors that affect the precipitation of magnesium carbonate, such as PAM concentration, reaction temperature, and stirring speed, were investigated comprehensively. Scanning electron microscopy (SEM) and X-ray powder diffraction (XRD) methods were used to characterize the carbonate precipitate products. PAM concentration, reaction temperature, and stirring speed have significant effects on the morphology of the carbonate products. The product weight increases slightly with the increase in the amount of PAM added, but decreases slightly with the increase in the reaction temperature, and is almost irrelevant to the stirring speed. The products obtained at 25 and 50 degrees C were all identified as nesquehonite, MgCO(3 center dot)3H(2)O. At 75 degrees C an unidentified amorphous product forms. The use of an additive is found to be an effective method to adjust the morphology of magnesium carbonate. The information gained in this study would be helpful for the preparation of magnesium carbonate or other magnesium compounds with specific morphology. (C) 2010 Elsevier B.V. All rights reserved. The precipitation of magnesium carbonate by the reaction of MgCl(2) with Na(2)CO(3), under the influence of polyacrylamide (PAM) was studied. Factors that affect the precipitation of magnesium carbonate, such as PAM concentration, reaction temperature, and stirring speed, were investigated comprehensively. Scanning electron microscopy (SEM) and X-ray powder diffraction (XRD) methods were used to characterize the carbonate precipitate products. PAM concentration, reaction temperature, and stirring speed have significant effects on the morphology of the carbonate products. The product weight increases slightly with the increase in the amount of PAM added, but decreases slightly with the increase in the reaction temperature, and is almost irrelevant to the stirring speed. The products obtained at 25 and 50 degrees C were all identified as nesquehonite, MgCO(3 center dot)3H(2)O. At 75 degrees C an unidentified amorphous product forms. The use of an additive is found to be an effective method to adjust the morphology of magnesium carbonate. The information gained in this study would be helpful for the preparation of magnesium carbonate or other magnesium compounds with specific morphology. (C) 2010 Elsevier B.V. All rights reserved. |
| 收录类别 | SCI |
| 语种 | 英语 |
| 公开日期 | 2013-09-11 |
| 源URL | [http://ir.isl.ac.cn/handle/363002/1915]  |
| 专题 | 青海盐湖研究所_青海盐湖研究所知识仓储 青海盐湖研究所_盐湖资源与化学实验室 |
| 推荐引用方式 GB/T 7714 | Li, Quan,Ye, Xiushen,Wu, Zhijian,et al. Magnesium carbonate precipitation under the influence of polyacrylamide[J]. POWDER TECHNOLOGY,2010,200(1-2):46-51. |
| APA | Li, Quan,Ye, Xiushen,Wu, Zhijian,&Guo, Min.(2010).Magnesium carbonate precipitation under the influence of polyacrylamide.POWDER TECHNOLOGY,200(1-2),46-51. |
| MLA | Li, Quan,et al."Magnesium carbonate precipitation under the influence of polyacrylamide".POWDER TECHNOLOGY 200.1-2(2010):46-51. |
入库方式： OAI收割
来源：青海盐湖研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。