Internal friction and dielectric relaxation studies on the oxygen vacancy diffusion in the novel La2Mo2O9-based oxide-ion conductors
文献类型：期刊论文
| 刊名 | ACTA METALLURGICA SINICA
 |
| 出版日期 | 2003 |
| 卷号 | 39 |
| 关键词 | SOLID ELECTROLYTES DOPED LAGAO3 CONDUCTIVITY SELECTION oxide-ion conductor SOFC La2MO2O9 internal friction dielectric relaxation |
| ISSN号 | 0412-1961 |
| 其他题名 | Internal friction and dielectric relaxation studies on the oxygen vacancy diffusion in the novel La_2Mo_2O_9-based oxide-ion conductors |
| 英文摘要 | Both internal friction and dielectric relaxation techniques were applied to investigate the novel oxide-ion conductors La(2-x)A(x)Mo(2)O(9) (A=Ca, Bi, K; x=0-0.3). Two relaxation peaks associated with the short-distance diffusion of oxygen ions were observed on the curves of internal friction and dielectric loss versus temperature, indicating that there are at least two relaxation processes for oxygen ion diffusion. After doping La2Mo2O9 with different elements, both relaxation peaks shift toward higher temperature and the activation energy of oxygen ion diffusion increases, the height of the higher-temperature peak decreases while that of the lower-temperature peak increases slightly. After properly doping (e.g. 30%Ca, 5%Bi, or 5%K doping), the conductivity of doped La2Mo2O9 at low temperature increases in different degrees. Based on the experimental results and the crystalline structure, a physical picture for oxygen vacancy diffusion in La(2-x)A(x)Mo(2)O(9) samples is suggested. |
| 语种 | 英语 |
| CSCD记录号 | CSCD:1266984 |
| WOS记录号 | WOS:000186981500003 |
| 源URL | [http://ir.hfcas.ac.cn:8080/handle/334002/57053]  |
| 专题 | 中国科学院合肥物质科学研究院 |
| 推荐引用方式 GB/T 7714 | . Internal friction and dielectric relaxation studies on the oxygen vacancy diffusion in the novel La2Mo2O9-based oxide-ion conductors[J]. ACTA METALLURGICA SINICA,2003,39. |
| APA | (2003).Internal friction and dielectric relaxation studies on the oxygen vacancy diffusion in the novel La2Mo2O9-based oxide-ion conductors.ACTA METALLURGICA SINICA,39. |
| MLA | "Internal friction and dielectric relaxation studies on the oxygen vacancy diffusion in the novel La2Mo2O9-based oxide-ion conductors".ACTA METALLURGICA SINICA 39(2003). |
入库方式： OAI收割
来源：合肥物质科学研究院
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。