Effect of Annealing on the Microstructure and Properties of In-situ Cu-Nb Microcomposite Wires
文献类型：期刊论文
| 刊名 | ACTA METALLURGICA SINICA-ENGLISH LETTERS
 |
| 出版日期 | 2016 |
| 卷号 | 29 |
| 关键词 | MAGNETIC-PROPERTIES THERMAL-STABILITY COMPOSITE WIRES TRANSVERSE MAGNETORESISTANCE POLYCRYSTALLINE ALUMINUM INDUCED DIFFUSION FIELD RESISTIVITY COPPER RECRYSTALLIZATION Annealing Microstructure Magnetoresistance Hardness Cu-Nb microcomposite wire |
| ISSN号 | 1006-7191 |
| 其他题名 | Effect of Annealing on the Microstructure and Properties of In-situ Cu-Nb Microcomposite Wires |
| 英文摘要 | The effects of annealing on microstructure, magnetoresistance, and hardness of an in situ Cu-Nb microcomposite wire have been investigated. Neither changes in microstructure nor hardness were found until 500 degrees C. Particularly, microstructural change within the Nb films was observed in the annealed samples. The room-temperature magnetoresistivity was almost negligible, while magnetoresistivity at -196 degrees C increased with magnetic field. At temperature above 500 degrees C, recovery and recrystallization occurred, and both the resistance and hardness decreased. |
| 资助项目 | [National Natural Science Foundation of China] ; [Natural Science Foundation of Fujian Province of China] ; [Science and Technology Fund from Fujian Education Department of China] ; [US National Science Foundation] ; [State of Florida] |
| 语种 | 英语 |
| CSCD记录号 | CSCD:5742775 |
| 源URL | [http://ir.hfcas.ac.cn:8080/handle/334002/52406]  |
| 专题 | 中国科学院合肥物质科学研究院 |
| 推荐引用方式 GB/T 7714 | . Effect of Annealing on the Microstructure and Properties of In-situ Cu-Nb Microcomposite Wires[J]. ACTA METALLURGICA SINICA-ENGLISH LETTERS,2016,29. |
| APA | (2016).Effect of Annealing on the Microstructure and Properties of In-situ Cu-Nb Microcomposite Wires.ACTA METALLURGICA SINICA-ENGLISH LETTERS,29. |
| MLA | "Effect of Annealing on the Microstructure and Properties of In-situ Cu-Nb Microcomposite Wires".ACTA METALLURGICA SINICA-ENGLISH LETTERS 29(2016). |
入库方式： OAI收割
来源：合肥物质科学研究院
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。