Micro-mechanisms of fatigue damage in copper crystals
文献类型:期刊论文
作者 | Zhang, ZF; Duan, QQ; Wang, ZG |
刊名 | ACTA METALLURGICA SINICA
![]() |
出版日期 | 2005-11-01 |
卷号 | 41期号:11页码:1143-1149 |
关键词 | copper crystal fatigue crack persistent slip band (PSB) deformation band (DB) grain boundary (GB) |
ISSN号 | 0412-1961 |
通讯作者 | Zhang, ZF(zhfzhang@imr.ac.cn) |
英文摘要 | Micro-mechanisms of fatigue damage in copper single-, bi- and poly-crystals were summarized in the present paper. A number of investigations reveal that fatigue crack mainly initiates along persistent slip bands (PSBs) in copper single crystals at low or medium strain range, however, nucleates along coarse deformation bands (DBs) at high strain range. For copper bi-crystals, various large-angle grain boundaries (GBs) are always the preferential sites for the nucleation and propagation of fatigue cracks while the low-angle GBs do not lead to fatigue cracking during fatigue. Fatigue cracks mainly nucleated along large-angle GBs, sometimes along PSBs in polycrystalline copper, however, the initiation of fatigue crack at twin boundaries (TBs) was not observed due to the compatible slip deformation across the TBs. |
WOS研究方向 | Metallurgy & Metallurgical Engineering |
语种 | 英语 |
WOS记录号 | WOS:000233702000005 |
出版者 | SCIENCE PRESS |
源URL | [http://ir.imr.ac.cn/handle/321006/84123] ![]() |
专题 | 金属研究所_中国科学院金属研究所 |
通讯作者 | Zhang, ZF |
作者单位 | Chinese Acad Sci, Inst Met Res, Shanyang Natl Lab Mat Sci, Shenyang 110016, Peoples R China |
推荐引用方式 GB/T 7714 | Zhang, ZF,Duan, QQ,Wang, ZG. Micro-mechanisms of fatigue damage in copper crystals[J]. ACTA METALLURGICA SINICA,2005,41(11):1143-1149. |
APA | Zhang, ZF,Duan, QQ,&Wang, ZG.(2005).Micro-mechanisms of fatigue damage in copper crystals.ACTA METALLURGICA SINICA,41(11),1143-1149. |
MLA | Zhang, ZF,et al."Micro-mechanisms of fatigue damage in copper crystals".ACTA METALLURGICA SINICA 41.11(2005):1143-1149. |
入库方式: OAI收割
来源:金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。