Fatigue behavior comparison of ecaped Al-Cu alloy under stress and strain control
文献类型：期刊论文
| 作者 | Li, YJ; Liu, SM; Wu, SD; Zhang, ZF; Wang, ZG |
| 刊名 | ACTA METALLURGICA SINICA
 |
| 出版日期 | 2005-04-11 |
| 卷号 | 41期号:4页码:380-384 |
| 关键词 | equal channel angular pressing (ECAP) Al-0.7%Cu alloy cyclic softening shear bands fatigue |
| ISSN号 | 0412-1961 |
| 通讯作者 | Zhang, ZF() |
| 英文摘要 | Fatigue life, surface deformation morphology, fatigue cracking and fatigue fractography of Al-0.7%Cu (mass fraction) alloy, produced by equal channel angular pressing (ECAP) for 4 passes, were investigated under constant stress or plastic strain control. It is shown that the specimens displayed obvious cyclic softening, which caused some difference in fatigue life at low or high stress range under constant stress and strain conditions. The plastic strain is carried either by shear bands only, or by shear bands and deformation bands, in the specimens fatigued under strain control. Consequently, fatigue cracks nucleated either along shear bands or along deformation bands. However, the plastic strain only localized in the shear bands of the specimens under stress control, as a result, leading to shearing fatigue cracking. The fatigue fractography consists of several different zones, including fatigue crack initiation, slow, fast propagation and final fracture. |
| WOS研究方向 | Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| WOS记录号 | WOS:000228756900009 |
| 出版者 | SCIENCE CHINA PRESS |
| 源URL | [http://ir.imr.ac.cn/handle/321006/84835]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Zhang, ZF |
| 作者单位 | Chinese Acad Sci, Inst Met Res, Shenyang Natl Lab Mat Sci, Shenyang 110016, Peoples R China |
| 推荐引用方式 GB/T 7714 | Li, YJ,Liu, SM,Wu, SD,et al. Fatigue behavior comparison of ecaped Al-Cu alloy under stress and strain control[J]. ACTA METALLURGICA SINICA,2005,41(4):380-384. |
| APA | Li, YJ,Liu, SM,Wu, SD,Zhang, ZF,&Wang, ZG.(2005).Fatigue behavior comparison of ecaped Al-Cu alloy under stress and strain control.ACTA METALLURGICA SINICA,41(4),380-384. |
| MLA | Li, YJ,et al."Fatigue behavior comparison of ecaped Al-Cu alloy under stress and strain control".ACTA METALLURGICA SINICA 41.4(2005):380-384. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。