Electrochemical behaviors of corrosion of LY12 aluminum alloy/passivation film/epoxy coatings composite electrodes

文献类型:期刊论文

作者Zhang, JT; Hu, JM; Zhang, JQ; Cao, CN
刊名ACTA METALLURGICA SINICA
出版日期2006-05-11
卷号42期号:5页码:528-532
关键词aluminum alloy passivation epoxy coating corrosion EIS
ISSN号0412-1961
通讯作者Hu, JM()
英文摘要The corrosion performance of LY12 aluminum alloys/passivation film/epoxy coatings in NaCl solution was characterized by electrochemical impedance spectroscopy (EIS). The results showed that the impedances of composite electrodes continuously increased with increasing of immersion time. In the beginning of immersion, the diffusion impedance emerged in the impedance spectroscopy of composite electrode, which was considered to result from the mass transport behavior of solving products of passivation film prepared on metal substrates. The observation of scanning electron microscope (SEM) indicated that the chromate conversion film presented the obvious crack morphology on metal substrates, which is favourable the solved chromate for penetrating through the film and passivate the metal substrate surface. This may be the possible reason of the continuous increase in impedance in composite electrodes.
WOS研究方向Metallurgy & Metallurgical Engineering
语种英语
WOS记录号WOS:000237981200016
出版者SCIENCE CHINA PRESS
源URL[http://ir.imr.ac.cn/handle/321006/88653]  
专题金属研究所_中国科学院金属研究所
通讯作者Hu, JM
作者单位1.Changzhou Inst Technol, Dept Chem, Changzhou 213002, Peoples R China
2.Zhejiang Univ, Dept Chem, Hangzhou 310027, Peoples R China
3.Chinese Acad Sci, Inst Met Res, State Key Lab Corros & Protect, Shenyang 110016, Peoples R China
推荐引用方式
GB/T 7714
Zhang, JT,Hu, JM,Zhang, JQ,et al. Electrochemical behaviors of corrosion of LY12 aluminum alloy/passivation film/epoxy coatings composite electrodes[J]. ACTA METALLURGICA SINICA,2006,42(5):528-532.
APA Zhang, JT,Hu, JM,Zhang, JQ,&Cao, CN.(2006).Electrochemical behaviors of corrosion of LY12 aluminum alloy/passivation film/epoxy coatings composite electrodes.ACTA METALLURGICA SINICA,42(5),528-532.
MLA Zhang, JT,et al."Electrochemical behaviors of corrosion of LY12 aluminum alloy/passivation film/epoxy coatings composite electrodes".ACTA METALLURGICA SINICA 42.5(2006):528-532.

入库方式: OAI收割

来源:金属研究所

浏览0
下载0
收藏0
其他版本

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。