Electrochemical hydrogen storage in LaNi4.25Al0.75 alloys: A comparative study between film and powder materials
文献类型：期刊论文
| 作者 | Wang, Z. M.1; Li, Chi Ying Vanessa2; Zhou, Huaiying1; Liu, Shi3; Chan, S. L. I.2 |
| 刊名 | MATERIALS CHARACTERIZATION
 |
| 出版日期 | 2008-04-01 |
| 卷号 | 59期号:4页码:468-472 |
| 关键词 | LaNi4.25Al0.75 film LaNi4.25Al0.75 powder magnetron sputtering electrochemical hydrogen storage properties |
| ISSN号 | 1044-5803 |
| DOI | 10.1016/j.matchar.2007.04.020 |
| 通讯作者 | Wang, Z. M.(zmwang@guet.edu.cn) |
| 英文摘要 | A comparison is made of the electrochemical and structural properties of LaNi4.25Al0.75 alloys in thin film and powder forms. X-ray diffraction (XRD) revealed that both the LaNi4.25Al0.75 thin film and powder materials are crystalline. Atomic force microscopy (AFM) and focused ion beam microscopy (FIB) proved that the film appeared to have a hill-like surface morphology, but was rather dense with a thickness of about 4.2 mu m. Simulated battery tests indicate that both exhibit similar electrochemical behavior, possibly due to their crystal structure, as it requires a primary activation to reach its fully active state. However it took a longer activation period for the film to be activated; an apparent initial decrease of charging voltage with cycle number was observed, as were abnormal discharge processes during activation. After 30 charge/discharge cycles, small needle-shaped aluminium oxide particles were formed on both the powder and film surfaces. (c) 2007 Published by Elsevier Inc. |
| WOS研究方向 | Materials Science |
| 语种 | 英语 |
| WOS记录号 | WOS:000253933600020 |
| 出版者 | ELSEVIER SCIENCE INC |
| 源URL | [http://ir.imr.ac.cn/handle/321006/94837]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Wang, Z. M. |
| 作者单位 | 1.Guilin Univ Elect Technol, Ctr Mat Sci & Engn, Guilin 541004, Guangxi, Peoples R China 2.Univ New S Wales, Sch Mat Sci & Engn, Sydney, NSW 2052, Australia 3.Chinese Acad Sci, Inst Met Res, Beijing 100864, Peoples R China |
| 推荐引用方式 GB/T 7714 | Wang, Z. M.,Li, Chi Ying Vanessa,Zhou, Huaiying,et al. Electrochemical hydrogen storage in LaNi4.25Al0.75 alloys: A comparative study between film and powder materials[J]. MATERIALS CHARACTERIZATION,2008,59(4):468-472. |
| APA | Wang, Z. M.,Li, Chi Ying Vanessa,Zhou, Huaiying,Liu, Shi,&Chan, S. L. I..(2008).Electrochemical hydrogen storage in LaNi4.25Al0.75 alloys: A comparative study between film and powder materials.MATERIALS CHARACTERIZATION,59(4),468-472. |
| MLA | Wang, Z. M.,et al."Electrochemical hydrogen storage in LaNi4.25Al0.75 alloys: A comparative study between film and powder materials".MATERIALS CHARACTERIZATION 59.4(2008):468-472. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。