IMPROVEMENT OF MECHANICAL PROPERTIES OF STEEL 1Cr13Mn13 BY ELECTROPULSING WITH HIGH DENSITY
文献类型：期刊论文
| 作者 | Zhao Yuanyun; Wang Baoquan; Guo Jingdong |
| 刊名 | ACTA METALLURGICA SINICA
 |
| 出版日期 | 2009-11-11 |
| 卷号 | 45期号:11页码:1325-1329 |
| 关键词 | steel 1Cr13Mn13 heat treatment electropulsing mechanical property martensite refinement |
| ISSN号 | 0412-1961 |
| 通讯作者 | Guo Jingdong(jdguo@imr.ac.cn) |
| 英文摘要 | Steel 1Cr13Mn13 was treated by electropulsing (EP) with high density after annealing+furnace cooling (AF) or solution+oil quenching+tempering (SOT). Tensile experiments show that the mechanical properties of the sample treated by SOT+EP process with a, maximum current intensity about 8.46 kA/mm(2) were greatly improved, compared with the sample only treated by SOT process, its tensile strength and elongation increased from (1250 +/- 10) MPa and (20 +/- 1)% to 1400 MPa and 53%, respectively. Metallographs show that the equiaxed grains formed under high temperature solid solution treatment were remained in both the SOT and SOT+EP samples. But the coarse lamellar martensite in the SOT sample was greatly refined after EP treatment. As the samples were treated by EP treatment, they successively underwent a rapidly "heating-cooling" process with a heating time less than 0.001 s and a cooling time less than 0.6 s, resulting in a successive phase transformation of alpha' -> gamma -> alpha'. The lamellar alpha' martensites formed during rapidly cooling process have more refined size than that of the primary martensite laths, which further enhanced the tensile ductility and tensile strength of steel 1Cr13Mn13 Moreover, the maximum value of current intensity for each EP treatment can also influence the mechanical properties of the samples by controlling the amount of the a' phase in the transformation. A higher current intensity usually produces much more amount of a' phase with smaller lamellar size and the mechanical properties of the samples are more improved. But if the maximum current intensity is much higher than an optimal range about 8.30-8.46 kA/mm(2), the sample is overheated and the mechanical properties will be lowered. |
| 资助项目 | National Basic Research Program of China[2004CB6.19306] |
| WOS研究方向 | Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| WOS记录号 | WOS:000272502600008 |
| 出版者 | SCIENCE PRESS |
| 资助机构 | National Basic Research Program of China |
| 源URL | [http://ir.imr.ac.cn/handle/321006/96094]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Guo Jingdong |
| 作者单位 | Chinese Acad Sci, Inst Met Res, Shenyang Natl Lab Mat Sci, Shenyang 110016, Peoples R China |
| 推荐引用方式 GB/T 7714 | Zhao Yuanyun,Wang Baoquan,Guo Jingdong. IMPROVEMENT OF MECHANICAL PROPERTIES OF STEEL 1Cr13Mn13 BY ELECTROPULSING WITH HIGH DENSITY[J]. ACTA METALLURGICA SINICA,2009,45(11):1325-1329. |
| APA | Zhao Yuanyun,Wang Baoquan,&Guo Jingdong.(2009).IMPROVEMENT OF MECHANICAL PROPERTIES OF STEEL 1Cr13Mn13 BY ELECTROPULSING WITH HIGH DENSITY.ACTA METALLURGICA SINICA,45(11),1325-1329. |
| MLA | Zhao Yuanyun,et al."IMPROVEMENT OF MECHANICAL PROPERTIES OF STEEL 1Cr13Mn13 BY ELECTROPULSING WITH HIGH DENSITY".ACTA METALLURGICA SINICA 45.11(2009):1325-1329. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。