Isothermal oxidation behavior of Ti3Al-based alloy at 700-1000 degrees C in air
文献类型：期刊论文
| 作者 | Qian Yu-hai1,2; Li Mei-shuan1; Lu Bin1 |
| 刊名 | TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA
 |
| 出版日期 | 2009-06-01 |
| 卷号 | 19期号:3页码:525-529 |
| 关键词 | oxidation resistance Ti3Al-based intermetallic alloy oxidation kinetics |
| ISSN号 | 1003-6326 |
| DOI | 10.1016/S1003-6326(08)60306-4 |
| 通讯作者 | Qian Yu-hai(yhqian@baosteel.com) |
| 英文摘要 | The isothermal oxidation behavior of a Ti3Al-based alloy (Ti-24Al-14Nb-3V-0.5Mo-0.3Si, molar fraction, %) at 700-1000 degrees C in air was investigated. The oxidation kinetics of tested alloy approximately obeys the parabolic law, which shows that the oxidation process is dominated by the diffusion of ions. The oxidation diffusion activity energy is 241.32 kJ/mol. The tested alloy exhibits good oxidation resistance at 700 degrees C. However, when the temperature is higher than 900 degrees C, the oxidation resistance becomes poor. The XRD results reveal that the oxide product consists of a mixture of TiO2 and Al2O3. Serious crack and spallation of oxide scale occur during cooling procedure after being exposed at 1000 degrees C in air for 16 h. According to the analysis of SEM/EDS and XRD, it is concluded that the Al2O3 oxide forms at the initially transient oxidation stage and most of it keeps in the outer oxide layer during the subsequent oxidation procedure. |
| 资助项目 | National Natural Science Foundation of China[50771099] |
| WOS研究方向 | Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| WOS记录号 | WOS:000266892200003 |
| 出版者 | ELSEVIER SCIENCE BV |
| 资助机构 | National Natural Science Foundation of China |
| 源URL | [http://ir.imr.ac.cn/handle/321006/96417]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Qian Yu-hai |
| 作者单位 | 1.Chinese Acad Sci, Inst Met Res, Shenyang Natl Lab Mat Sci, Shenyang 110016, Peoples R China 2.Baoshan Iron & Steel Co Ltd, R&D Ctr, Shanghai 201900, Peoples R China |
| 推荐引用方式 GB/T 7714 | Qian Yu-hai,Li Mei-shuan,Lu Bin. Isothermal oxidation behavior of Ti3Al-based alloy at 700-1000 degrees C in air[J]. TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA,2009,19(3):525-529. |
| APA | Qian Yu-hai,Li Mei-shuan,&Lu Bin.(2009).Isothermal oxidation behavior of Ti3Al-based alloy at 700-1000 degrees C in air.TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA,19(3),525-529. |
| MLA | Qian Yu-hai,et al."Isothermal oxidation behavior of Ti3Al-based alloy at 700-1000 degrees C in air".TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA 19.3(2009):525-529. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。