Preparation of TiAl3-Al composite coating by cold spraying
文献类型:期刊论文
作者 | Shen Li; Kong Ling-yan; Xiong Tian-ying; Du Hao; Li Tie-fan |
刊名 | TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA
![]() |
出版日期 | 2009-08-01 |
卷号 | 19期号:4页码:879-882 |
关键词 | cold spraying TiAl3-Al composite coating orthorhombic Ti2AlNb alloy high temperature oxidation |
ISSN号 | 1003-6326 |
DOI | 10.1016/S1003-6326(08)60369-6 |
通讯作者 | Xiong Tian-ying(tyxiong@imr.ac.cn) |
英文摘要 | TiAl3-Al coating was deposited on orthorhombic Ti2AlNb alloy substrate by cold spraying with the mixture of pure Al and Ti as the feedstock powder at a fixed molar ratio of 3:1 when the spraying distance, gas temperature and gas pressure for the process were 10 mm, 250 degrees C and 1.8 MPa, respectively. The as-sprayed coating was then subjected to heat treatment at 630 degrees C in argon atmosphere for 5 h at a heating rate of 3 degrees C/min and an argon gas flow rate of 40 mL/min. The obtained TiAl3-Al composite coating is about 212 mu m with a density of 3.16 g/cm(3) and a porosity of 14.69% in general. The microhardness and bonding strength for the composite coating are HV525 and 27.12 MPa. |
WOS研究方向 | Metallurgy & Metallurgical Engineering |
语种 | 英语 |
WOS记录号 | WOS:000269099300020 |
出版者 | ELSEVIER SCIENCE BV |
源URL | [http://ir.imr.ac.cn/handle/321006/97587] ![]() |
专题 | 金属研究所_中国科学院金属研究所 |
通讯作者 | Xiong Tian-ying |
作者单位 | Chinese Acad Sci, State Key Lab Corros & Protect, Inst Met Res, Shenyang 110016, Peoples R China |
推荐引用方式 GB/T 7714 | Shen Li,Kong Ling-yan,Xiong Tian-ying,et al. Preparation of TiAl3-Al composite coating by cold spraying[J]. TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA,2009,19(4):879-882. |
APA | Shen Li,Kong Ling-yan,Xiong Tian-ying,Du Hao,&Li Tie-fan.(2009).Preparation of TiAl3-Al composite coating by cold spraying.TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA,19(4),879-882. |
MLA | Shen Li,et al."Preparation of TiAl3-Al composite coating by cold spraying".TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA 19.4(2009):879-882. |
入库方式: OAI收割
来源:金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。