Preparation and Luminescence Characteristics of BaHfO3:Ce Nanoparticles by the Process of Solid-State Reaction
文献类型：期刊论文
| 作者 | Yin Kai1,2; Ma Wei-Min2; Wen Lei3; Shen Shi-Fei1; Wang Hua-Dong1; Guo Yi-Fen1 |
| 刊名 | CHINESE JOURNAL OF INORGANIC CHEMISTRY
 |
| 出版日期 | 2009-07-10 |
| 卷号 | 25期号:7页码:1248-1253 |
| 关键词 | scintillant BaHfO3:Ce nanoparticles solid-state reaction process excitation spectrum emission spectrum |
| ISSN号 | 1001-4861 |
| 通讯作者 | Ma Wei-Min(maweimin56@163.com) |
| 英文摘要 | BaHfO3:Ce nanoparticles were synthesized by the process of solid-state reaction. Both XRD and SEM were adopted to analyze the phase change and the characteristics of BaHfO3:Ce nano-powders during calcining process. Excitation and emission spectra were analyzed separately with the fluorescence photometer. The result shows that the average diameter of the BaHfO3:Ce nano-powders being approximate to spherical morphology is about 30 nm and the powders have good dispersibility after calcining at 1000 degrees C for 2 h. It also shows that there is no change happened on the cubic crystal structure even though a little amount of Ce3+ ion added to the powders can lead to the lattice distortion of BaHfO3 matrix material. The excitation spectrum of BaHfO3: Ce nanoparticles has two excitation peaks separately at 396 nm and 446 nm points. The emission spectrum excited by the 396 nm light consists of two emission bands, peaking at 531 nm and 591 run, respectively, the emission character of which changes from the 5d -> F-2(5/2) to 5d -> F-2(7/2) transitions of Ce3+ cation. When the emission spectrum is excited by the 446 nm light, only one wide emission peak at 591 nm point exists and the other one at around 531 nm becomes flat. When the Ce3+ dopant content is 0.9%(molar fraction), the figure of the emission peak reaches its highest point. This figure, however, drops when The Ce3+ dopant content is 1.1%( molar fraction), which is resulted from the concentraction quenching. |
| WOS研究方向 | Chemistry |
| 语种 | 英语 |
| WOS记录号 | WOS:000268841500020 |
| 出版者 | CHINESE CHEMICAL SOC |
| 源URL | [http://ir.imr.ac.cn/handle/321006/99432]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Ma Wei-Min |
| 作者单位 | 1.Shenyang Univ, Coll Mech Engn, Shenyang 110044, Peoples R China 2.Shenyang Inst Chem Technol, Sch Mat Sci & Engn, Shenyang 110142, Peoples R China 3.Chinese Acad Sci, Shenyang Natl Lab Mat Sci, Inst Met Res, Shenyang 110016, Peoples R China |
| 推荐引用方式 GB/T 7714 | Yin Kai,Ma Wei-Min,Wen Lei,et al. Preparation and Luminescence Characteristics of BaHfO3:Ce Nanoparticles by the Process of Solid-State Reaction[J]. CHINESE JOURNAL OF INORGANIC CHEMISTRY,2009,25(7):1248-1253. |
| APA | Yin Kai,Ma Wei-Min,Wen Lei,Shen Shi-Fei,Wang Hua-Dong,&Guo Yi-Fen.(2009).Preparation and Luminescence Characteristics of BaHfO3:Ce Nanoparticles by the Process of Solid-State Reaction.CHINESE JOURNAL OF INORGANIC CHEMISTRY,25(7),1248-1253. |
| MLA | Yin Kai,et al."Preparation and Luminescence Characteristics of BaHfO3:Ce Nanoparticles by the Process of Solid-State Reaction".CHINESE JOURNAL OF INORGANIC CHEMISTRY 25.7(2009):1248-1253. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。