EVOLUTIONS OF MICROSTRUCTURES AND MECHANICAL PROPERTIES OF TWO CAST Ni-BASED SUPERALLOYS DURING LONG-TERM THERMAL EXPOSURE
文献类型：期刊论文
| 作者 | Qin Xuezhi; Guo Jianting; Yuan Chao; Hou Jieshan; Zhou Lanzhang; Ye Hengqiang |
| 刊名 | ACTA METALLURGICA SINICA
 |
| 出版日期 | 2010-02-11 |
| 卷号 | 46期号:2页码:213-220 |
| 关键词 | Ni-based superalloy long-term thermal exposure microstructural stability mechanical property |
| ISSN号 | 0412-1961 |
| DOI | 10.3724/SP.J.1037.2009.00449 |
| 通讯作者 | Qin Xuezhi() |
| 英文摘要 | K452 and K446 alloys are two newly developed Ni-based cast superalloys, designed for microstructural component, applications of gas turbines in marine and industrial fields The two alloys perform well under laboratory conditions with good fatigue resistance, hot-corrosion resistance. and tensile- and stress-rupture properties, in addition to being completely oxidation resistant up to 900 degrees C However, due to the high contents of Cr, W and Mo, both K452 and K446 alloys tend to experience a severe microstructural degeneration when exposed at elevated temperatures In this paper, the microstructural stabilities and their influences oil the mechanical properties of the two alloys were comparatively examined during thermal exposure at 800-900 degrees C for 1 x 10(3)-1 x 10(4) h It is found that the gamma' phases in the two alloys keep coarsening and are both spherical during the whole exposure The coarsening rate of the gamma' phase in K446 is in general faster than that in K452, the probable reason of which is that elements diffuse faster in K446 than in K452 due to the different heat treatment regimes they suffered The thermal stabilities of primary MC carbides are closely related to the chemical compositions of both the carbides and the alloys The carbide in K452 is instable and tends to completely decompose via three different reactions, whereas the carbide in K446 is stable and degenerates only to a tiny degree mainly via one reaction Primary MC degeneration in K452 releases a significant amount of C into the supersaturated gamma matrix, facilitating the formation of M(23)C(6) throughout the alloy, whereas the, MC degeneration in K446 hardly releases C into the gamma matrix so that the mu phase precipitates everywhere due to the lack of C It seems that the kind of the phase precipitated from the supersaturated matrix during thermal exposure of service is dependent oil the stability of primary MC in K452 the blocky, closely spaced grain boundary M(23)C(6) particles engulfed in gamma' is the optimal structure of grain boundary, where a stress rupture life peak occurs, whereas in K446 the precipitation of a significant amount of mu phase degrades sharply the stress-rupture life. |
| WOS研究方向 | Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| WOS记录号 | WOS:000275347700015 |
| 出版者 | SCIENCE PRESS |
| 源URL | [http://ir.imr.ac.cn/handle/321006/100199]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Qin Xuezhi |
| 作者单位 | Chinese Acad Sci, Inst Met Res, Shenyang 110016, Peoples R China |
| 推荐引用方式 GB/T 7714 | Qin Xuezhi,Guo Jianting,Yuan Chao,et al. EVOLUTIONS OF MICROSTRUCTURES AND MECHANICAL PROPERTIES OF TWO CAST Ni-BASED SUPERALLOYS DURING LONG-TERM THERMAL EXPOSURE[J]. ACTA METALLURGICA SINICA,2010,46(2):213-220. |
| APA | Qin Xuezhi,Guo Jianting,Yuan Chao,Hou Jieshan,Zhou Lanzhang,&Ye Hengqiang.(2010).EVOLUTIONS OF MICROSTRUCTURES AND MECHANICAL PROPERTIES OF TWO CAST Ni-BASED SUPERALLOYS DURING LONG-TERM THERMAL EXPOSURE.ACTA METALLURGICA SINICA,46(2),213-220. |
| MLA | Qin Xuezhi,et al."EVOLUTIONS OF MICROSTRUCTURES AND MECHANICAL PROPERTIES OF TWO CAST Ni-BASED SUPERALLOYS DURING LONG-TERM THERMAL EXPOSURE".ACTA METALLURGICA SINICA 46.2(2010):213-220. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。