The effect of H2S concentration on the corrosion behavior of carbon steel at 90 degrees C
文献类型：期刊论文
| 作者 | Tang, Junwen1; Shao, Yawei1,2; Guo, Jinbiao3; Zhang, Tao1,2; Meng, Guozhe1,2; Wang, Fuhui1,2 |
| 刊名 | CORROSION SCIENCE
 |
| 出版日期 | 2010-06-01 |
| 卷号 | 52期号:6页码:2050-2058 |
| 关键词 | Steel Weight loss SEM XRD Acid corrosion |
| ISSN号 | 0010-938X |
| DOI | 10.1016/j.corsci.2010.02.004 |
| 通讯作者 | Shao, Yawei(shaoyawei@hrbeu.edu.cn) |
| 英文摘要 | The electrochemical behavior of SAE-1020 carbon steel in 0.25 M Na2SO4 solution containing different concentrations of H2S at 90 degrees C was investigated using the methods of weight loss, electrochemical measurements, scanning electron microscopy (SEM) and X-ray diffraction (XRD). The results showed that the corrosion rate of carbon steel increased significantly with the increase of H2S concentration. H2S accelerated the corrosion rate of SAE-1020 carbon steel by a promoted hydrogen evolution reaction. Severe corrosion cavities were observed on the carbon steel surface in the solutions containing H2S due to cementites stripped off from the grain boundary. The loose corrosion products formed on the steel surfaces were composed of mackinawite. (C) 2010 Elsevier Ltd. All rights reserved. |
| 资助项目 | Academe of Lanzhou Petrochemic Company ; CNPC |
| WOS研究方向 | Materials Science ; Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| WOS记录号 | WOS:000277953000020 |
| 出版者 | PERGAMON-ELSEVIER SCIENCE LTD |
| 资助机构 | Academe of Lanzhou Petrochemic Company ; CNPC |
| 源URL | [http://ir.imr.ac.cn/handle/321006/102356]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Shao, Yawei |
| 作者单位 | 1.Harbin Engn Univ, Minist Educ, Key Lab Superlight Mat & Surface Technol, Corros & Protect Lab, Harbin 150001, Peoples R China 2.Chinese Acad Sci, Inst Met Res, State Key Lab Corros & Protect, Shenyang 110015, Peoples R China 3.Acad Lanzhou Petrochem Co, CNPC, Lanzhou 730060, Peoples R China |
| 推荐引用方式 GB/T 7714 | Tang, Junwen,Shao, Yawei,Guo, Jinbiao,et al. The effect of H2S concentration on the corrosion behavior of carbon steel at 90 degrees C[J]. CORROSION SCIENCE,2010,52(6):2050-2058. |
| APA | Tang, Junwen,Shao, Yawei,Guo, Jinbiao,Zhang, Tao,Meng, Guozhe,&Wang, Fuhui.(2010).The effect of H2S concentration on the corrosion behavior of carbon steel at 90 degrees C.CORROSION SCIENCE,52(6),2050-2058. |
| MLA | Tang, Junwen,et al."The effect of H2S concentration on the corrosion behavior of carbon steel at 90 degrees C".CORROSION SCIENCE 52.6(2010):2050-2058. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。