Corrosion failure analysis of pure nickel thermocouple sheath used in BaTiO3 hydrothermal synthesis reactor
文献类型：期刊论文
| 作者 | Zhong, X. Y.1; Wu, X. Q.1; Han, E. H.1; Song, X. B.2 |
| 刊名 | ENGINEERING FAILURE ANALYSIS
 |
| 出版日期 | 2010-09-01 |
| 卷号 | 17期号:6页码:1404-1412 |
| 关键词 | Corrosion failure analysis Crevice corrosion Pure Ni High temperature High pressure |
| ISSN号 | 1350-6307 |
| DOI | 10.1016/j.engfailanal.2010.04.006 |
| 通讯作者 | Wu, X. Q.(xqwu@imr.ac.cn) |
| 英文摘要 | This paper presents corrosion failure analysis on a commercial pure nickel thermocouple sheath used in BaTiO3 hydrothermal synthesis reactor. Detailed investigations of the corrosion products have been performed using stereomicroscope, X-ray diffraction, scanning electron microscopy and energy-dispersive X-ray spectroscopy. It was found that the corrosion failure of the sheath was mainly due to general corrosion and crevice corrosion of pure nickel, and the main corrosion products were Ni(OH)(2). Many cracks were observed inside the corrosion products and along the interfaces between the corrosion products and metal matrix. BaTiO3 particles were deposited as parallel white bands along the above cracks inside the corrosion products. Chloride ions also entered the cracks or crevices, resulting in the acidification inside the crevice and aggravated the attack of nickel matrix. Some recommendations to prevent/minimize future similar corrosion failures were proposed. (C) 2010 Elsevier Ltd. All rights reserved. |
| 资助项目 | Science and Technology Foundation of China[50871113] ; Special Funds for the Major State Basic Research[2006CB605001] ; Institute of Metal Research (IMR), Chinese Academy of Sciences (CAS) |
| WOS研究方向 | Engineering ; Materials Science |
| 语种 | 英语 |
| WOS记录号 | WOS:000280885100014 |
| 出版者 | PERGAMON-ELSEVIER SCIENCE LTD |
| 资助机构 | Science and Technology Foundation of China ; Special Funds for the Major State Basic Research ; Institute of Metal Research (IMR), Chinese Academy of Sciences (CAS) |
| 源URL | [http://ir.imr.ac.cn/handle/321006/102728]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Wu, X. Q. |
| 作者单位 | 1.Chinese Acad Sci, State Key Lab Corros & Protect, Inst Met Res, Shenyang 110016, Peoples R China 2.Shandong Sinocera Funct Mat Co Ltd, Dongying 257091, Peoples R China |
| 推荐引用方式 GB/T 7714 | Zhong, X. Y.,Wu, X. Q.,Han, E. H.,et al. Corrosion failure analysis of pure nickel thermocouple sheath used in BaTiO3 hydrothermal synthesis reactor[J]. ENGINEERING FAILURE ANALYSIS,2010,17(6):1404-1412. |
| APA | Zhong, X. Y.,Wu, X. Q.,Han, E. H.,&Song, X. B..(2010).Corrosion failure analysis of pure nickel thermocouple sheath used in BaTiO3 hydrothermal synthesis reactor.ENGINEERING FAILURE ANALYSIS,17(6),1404-1412. |
| MLA | Zhong, X. Y.,et al."Corrosion failure analysis of pure nickel thermocouple sheath used in BaTiO3 hydrothermal synthesis reactor".ENGINEERING FAILURE ANALYSIS 17.6(2010):1404-1412. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。