Anti-friction Behavior of Lead Perrhenate in a Broad Temperature Range
文献类型：期刊论文
| 作者 | Liu Lin-Lin; Li Shu; Liu Yang |
| 刊名 | JOURNAL OF INORGANIC MATERIALS
 |
| 出版日期 | 2010-11-01 |
| 卷号 | 25期号:11页码:1204-1208 |
| 关键词 | lead perrhenate anti-friction elevated temperature declined temperature |
| ISSN号 | 1000-324X |
| DOI | 10.3724/SP.J.1077.2010.01204 |
| 通讯作者 | Liu Lin-Lin(llliu@imr.ac.cn) |
| 英文摘要 | Extensive research efforts have been devoted to develop a new substance which could achieve effective lubrication in a broad temperature range. Pb(ReO(4))(2), composed of the double oxides of PbO and Re(2)O(7), exists in low shear strength. The anti-friction behavior of Pb(ReO(4))(2) was tested by Universal Micro-Tribotester (UMT-2M) with ball (Si(3)N(4)) on disc (superalloy) at elevated and declined temperature in the range of 22 degrees C to 600 degrees C. Composition of debris and morphologies of worn tracks were determined by X-ray diffraction (XRD) and scanning electron microscope (SEM), and contact resistance between the worn surface and steel ball was measured by UMT. The results show that Pb(ReO(4))(2) is a superior lubricant at elevated and declined temperatures, and the friction coefficient is much lower than that without lubricant. The superior lubricating properties should be attributed to the formation of an anti-frictional surface film. And higher temperature could result in the formation of a more complete and durable film. For Pb(ReO(4))(2) melts at 566 degrees C, the fused product is much easier to flow and generate a film which could separate the tribo-pairs perfectly. Subsequently, the lowest friction coefficient is gained at 600 degrees C, and good lubrication can be maintained till to 22 degrees C. |
| WOS研究方向 | Materials Science |
| 语种 | 英语 |
| WOS记录号 | WOS:000285404400017 |
| 出版者 | SCIENCE CHINA PRESS |
| 源URL | [http://ir.imr.ac.cn/handle/321006/102968]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Liu Lin-Lin |
| 作者单位 | Chinese Acad Sci, Inst Met Res, Shenyang 110016, Peoples R China |
| 推荐引用方式 GB/T 7714 | Liu Lin-Lin,Li Shu,Liu Yang. Anti-friction Behavior of Lead Perrhenate in a Broad Temperature Range[J]. JOURNAL OF INORGANIC MATERIALS,2010,25(11):1204-1208. |
| APA | Liu Lin-Lin,Li Shu,&Liu Yang.(2010).Anti-friction Behavior of Lead Perrhenate in a Broad Temperature Range.JOURNAL OF INORGANIC MATERIALS,25(11),1204-1208. |
| MLA | Liu Lin-Lin,et al."Anti-friction Behavior of Lead Perrhenate in a Broad Temperature Range".JOURNAL OF INORGANIC MATERIALS 25.11(2010):1204-1208. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。