Mg/Al REACTION AND MECHANICAL PROPERTIES OF Al ALLOY/Mg ALLOY FRICTION STIR WELDING JOINTS
文献类型：期刊论文
| 作者 | Wang Dong1; Liu Jie2; Xia Bolue1; Ma Zongyi1 |
| 刊名 | ACTA METALLURGICA SINICA
 |
| 出版日期 | 2010-05-11 |
| 卷号 | 46期号:5页码:589-594 |
| 关键词 | friction stir welding dissimilar alloy welding 6061 Al alloy AZ31 Mg alloy microstructure |
| ISSN号 | 0412-1961 |
| DOI | 10.3724/SP.J.1037.2009.00802 |
| 通讯作者 | Ma Zongyi(zyma@imr.ac.cn) |
| 英文摘要 | Mg alloys are increasingly used in aerospace, aircraft and automotives structures due to the low density and good damping properties, especially, the welding of Mg alloy to Al alloys is of practical importance for widening the application of Mg alloys. Although friction stir welding (FSW) has been used to join Mg and Al alloys, defect free joints are achieved only in the thin plate (less than 4 mm). In this paper, three ways of FSW of 6 mm thick 6061-T651 Al alloy and AZ31 Mg alloy plates, offsetting the pin to the seam between the two plates (M4A4), to the Mg alloy side 2 mm (M6A2) and to the Al alloy side 2 mm (A6M2), were studied. The aim is to examine the effects of the relative position between tool and plate on the microstructure and mechanical properties of FSW Mg/Al alloys joint. SEM and XRD analyses revealed the formations of intermetallics Mg(17)Al(12) and voids in the interface between Mg and Al alloy plates in the three FSW samples. The voids are resulted from the melting and subsequent solidification of eutectic. In the M4A4 and M6A2 samples, some Al are stirred into the Mg alloy side during FSW, forming the Mg(17)Al(12), whereas in the A6M2 sample, sonic Mg stirred into the Al alloy side are also transformed to the Mg(17)Al(12). Some fine pores are observed around the Mg(17)Al(12). The hardness of the nugget zone exhibits a slight increase due to the formation of a small amount of Mg(17)Al(12). The intermetallics and pores at the jointed interface decrease the strength of the joints significantly. |
| 资助项目 | National Outstanding Young Scientist Foundation[50525103] ; Chinese Academy of Sciences |
| WOS研究方向 | Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| WOS记录号 | WOS:000278475200011 |
| 出版者 | SCIENCE CHINA PRESS |
| 资助机构 | National Outstanding Young Scientist Foundation ; Chinese Academy of Sciences |
| 源URL | [http://ir.imr.ac.cn/handle/321006/103042]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Ma Zongyi |
| 作者单位 | 1.Chinese Acad Sci, Shenyang Natl Lab Mat Sci, Inst Met Res, Shenyang 110016, Peoples R China 2.Aviat Ind Corp China, Shenyang Liming Corp, Shenyang 110043, Peoples R China |
| 推荐引用方式 GB/T 7714 | Wang Dong,Liu Jie,Xia Bolue,et al. Mg/Al REACTION AND MECHANICAL PROPERTIES OF Al ALLOY/Mg ALLOY FRICTION STIR WELDING JOINTS[J]. ACTA METALLURGICA SINICA,2010,46(5):589-594. |
| APA | Wang Dong,Liu Jie,Xia Bolue,&Ma Zongyi.(2010).Mg/Al REACTION AND MECHANICAL PROPERTIES OF Al ALLOY/Mg ALLOY FRICTION STIR WELDING JOINTS.ACTA METALLURGICA SINICA,46(5),589-594. |
| MLA | Wang Dong,et al."Mg/Al REACTION AND MECHANICAL PROPERTIES OF Al ALLOY/Mg ALLOY FRICTION STIR WELDING JOINTS".ACTA METALLURGICA SINICA 46.5(2010):589-594. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。