EFFECTS OF DOUBLE EXTRUSION ON THE MICROSTRUCTURE AND TENSILE PROPERTY OF THE PM PROCESSED SiCp/2009Al COMPOSITES
文献类型：期刊论文
| 作者 | Liu Zhenyu; Wang Quanzhao; Xiao Bolue; Ma Zongyi; Liu Yue |
| 刊名 | ACTA METALLURGICA SINICA
 |
| 出版日期 | 2010-09-11 |
| 卷号 | 46期号:9页码:1121-1127 |
| 关键词 | powder metallurgy composite aluminum alloy double extrusion SiCp-poor band |
| ISSN号 | 0412-1961 |
| DOI | 10.3724/SP.J.1037.2010.00207 |
| 通讯作者 | Xiao Bolue(blxiao@imr.ac.cn) |
| 英文摘要 | Powder metallurgy (PM), as an important method of fabricating SiC particle reinforced aluminum matrix (SiCp/Al) composites, has advantages in obtaining good interfacial bonding and enhancing tensile strength over casting or infiltrating method. The primary process of the PM method involves mixing, compaction and subsequent secondary plastic deformation. Especially, secondary plastic deformation is an important process to destroy the oxidation film on the Al particle surfaces and enhance Al-SiC bonding. However, the incorporation of the SIC particles restricts plastic flow ability of the composite and makes it difficult to be subjected to heavy single-step plastic deformation, such as single hot extrusion, hot rolling or hot forging. Instead, multi-step deformation is a critical processing approach for the SiCp/Al composites with low deformability. However, the previous attentions were mostly focused on single-step processing, multi-step plastic deformation of the SiCp/Al composites was seldom discussed. In this paper, 20%SiCp/2009Al (volume fraction) composite was fabricated using a common PM method and the effects of double extrusion on the microstructure and tensile property of the composite were investigated. It is indicated that the double extrusion could refine the SiCp size, align the SiCp and increase the aspect ratio of the SiCp, but did not exert critical effects of the grain size and < 111 > texture of the matrix. However, the average distance between the SiCp along the extrusion direction increased after the double extrusion, more easily inducing a SiCp-poor band which aligned approximately perpendicularly to the extrusion direction. This resulted in a decrease in the strength and an increase in the elongation along the extrusion direction. |
| WOS研究方向 | Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| WOS记录号 | WOS:000282804800016 |
| 出版者 | SCIENCE PRESS |
| 源URL | [http://ir.imr.ac.cn/handle/321006/103102]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Xiao Bolue |
| 作者单位 | Chinese Acad Sci, Inst Met Res, Shenyang 110016, Peoples R China |
| 推荐引用方式 GB/T 7714 | Liu Zhenyu,Wang Quanzhao,Xiao Bolue,et al. EFFECTS OF DOUBLE EXTRUSION ON THE MICROSTRUCTURE AND TENSILE PROPERTY OF THE PM PROCESSED SiCp/2009Al COMPOSITES[J]. ACTA METALLURGICA SINICA,2010,46(9):1121-1127. |
| APA | Liu Zhenyu,Wang Quanzhao,Xiao Bolue,Ma Zongyi,&Liu Yue.(2010).EFFECTS OF DOUBLE EXTRUSION ON THE MICROSTRUCTURE AND TENSILE PROPERTY OF THE PM PROCESSED SiCp/2009Al COMPOSITES.ACTA METALLURGICA SINICA,46(9),1121-1127. |
| MLA | Liu Zhenyu,et al."EFFECTS OF DOUBLE EXTRUSION ON THE MICROSTRUCTURE AND TENSILE PROPERTY OF THE PM PROCESSED SiCp/2009Al COMPOSITES".ACTA METALLURGICA SINICA 46.9(2010):1121-1127. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。