ANALYSES OF SURFACE OXIDE FILMS ON ELECTROPOLISHED ALLOY 690TT AFTER IMMERSION FOR DIFFERENT TIMES
文献类型：期刊论文
| 作者 | Zhang Zhiming; Wang Jianqiu; Han En-Hou; Ke Wei |
| 刊名 | ACTA METALLURGICA SINICA
 |
| 出版日期 | 2011-07-11 |
| 卷号 | 47期号:7页码:831-838 |
| 关键词 | Ni base alloy 690TT eletropolishing treatment immersion time oxide film protective structure |
| ISSN号 | 0412-1961 |
| DOI | 10.3724/SP.J.1037.2011.00300 |
| 通讯作者 | Wang Jianqiu(wangjianqiu@imr.ac.cn) |
| 英文摘要 | The corrosion of Ni base alloys in high temperature and high pressure water is affected by samples surface statuses. The morphologies and structures of surface oxide films grown on electropolished (EP) alloy 690TT after immersion in the simulated hydrogenated primary water of pressured water reactors (PWRs) for different times were analyzed by AFM, SEM, TEM, EDS and XPS. After immersion for 15 and 35 h, the EP alloy 690TT samples were covered with columnar oxides. With the increase of the immersion time, the sample surfaces were covered with scattered big oxide particles and loose needle-like oxides. Regardless of the immersion time, the formed oxide films are composed of spinel oxides and metallic Ni. After immersion for 720, 1440 and 2160 h, the oxide films are composed of three layers: the outmost layer is the separated big oxide particles which are rich in Fe and Ni; the intermediate layer is the loose needle-like oxides rich in Ni; the inner layer is the continuous and compact Cr oxides. The peak decomposition of the XPS revealed that the Cr oxides in the inner layer are probably Cr(2)O(3). Only the inner layer in the oxide film could restrain the outward diffusion of metal atoms and also the inward diffusion of the oxygen atoms and then played the role of barrier layer well. Electropolishing treatment disadvantaged the fast growth of protective oxide film on alloy 690TT in the studied solution. The average corrosion rate of the inner layer does not decrease gradually with increasing the immersion time. After immersion for 2160 h, the oxide film still could not protect the matrix from further corrosion. |
| 资助项目 | National Basic Research Program of China[2011CB610502] ; National Natural Science Foundation of China[51025104] |
| WOS研究方向 | Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| WOS记录号 | WOS:000294980700011 |
| 出版者 | SCIENCE PRESS |
| 资助机构 | National Basic Research Program of China ; National Natural Science Foundation of China |
| 源URL | [http://ir.imr.ac.cn/handle/321006/103506]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Wang Jianqiu |
| 作者单位 | Chinese Acad Sci, Inst Met Res, State Key Lab Corros & Protect, Shenyang 110016, Peoples R China |
| 推荐引用方式 GB/T 7714 | Zhang Zhiming,Wang Jianqiu,Han En-Hou,et al. ANALYSES OF SURFACE OXIDE FILMS ON ELECTROPOLISHED ALLOY 690TT AFTER IMMERSION FOR DIFFERENT TIMES[J]. ACTA METALLURGICA SINICA,2011,47(7):831-838. |
| APA | Zhang Zhiming,Wang Jianqiu,Han En-Hou,&Ke Wei.(2011).ANALYSES OF SURFACE OXIDE FILMS ON ELECTROPOLISHED ALLOY 690TT AFTER IMMERSION FOR DIFFERENT TIMES.ACTA METALLURGICA SINICA,47(7),831-838. |
| MLA | Zhang Zhiming,et al."ANALYSES OF SURFACE OXIDE FILMS ON ELECTROPOLISHED ALLOY 690TT AFTER IMMERSION FOR DIFFERENT TIMES".ACTA METALLURGICA SINICA 47.7(2011):831-838. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。