INFLUENCE OF pH VALUES AND CORROSION PRODUCTS ON LOW CARBON STEEL CORROSION SUSCEPTIBILITY IN BORATE BUFFER SOLUTION
文献类型：期刊论文
| 作者 | Yang Jingfeng; Dong Junhua; Ke Wei; Chen Nan |
| 刊名 | ACTA METALLURGICA SINICA
 |
| 出版日期 | 2011-02-11 |
| 卷号 | 47期号:2页码:152-156 |
| 关键词 | borate buffer solution low carbon steel corrosion product active/passive potentiostat preparation |
| ISSN号 | 0412-1961 |
| DOI | 10.3724/SP.J.1037.2010.00439 |
| 通讯作者 | Dong Junhua(jhdong@imr.ac.cn) |
| 英文摘要 | Low carbon steel has been studied as one candidate material of the outer container used in the geological disposal of the high-level radioactive nuclear waste. The active/passive state of the steel is the most important factor in maintaining the service life of the container. The active state will ensure that the container achieve the designed life under general corrosion, and moreover, the passive state will degrade the container's life under stress corrosion cracking (SCC) caused by pitting corrosion. In the groundwater, a lot of chemical compositions have very complicated effects on the active/passive state of the low carbon steel. Among these factors, obviously, the pH values of the ground water and the corrosion products of the low carbon steel would be the most important factors. In this paper, the influences of pH values and corrosion products on the susceptibility of the low carbon steel in the deaerated borate buffer solutions were studied. The results showed that the corrosion product did not change the corrosion potential of the low carbon steel at a pH value of 8, which means that the steel was in the active state, while the corrosion product made the corrosion potentials of low carbon steel move to the passive state at pH values of 9 and 10. XPS and XRD analyses indicated that the corrosion products were composed of Fe(6)(OH)(12)B(4)O(7) and gamma-FeOOH. The low carbon steel with corrosion products was passivated more easily than the naked steel substrate. |
| 资助项目 | National Natural Science Foundation of China[51071160] |
| WOS研究方向 | Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| WOS记录号 | WOS:000288568700004 |
| 出版者 | SCIENCE CHINA PRESS |
| 资助机构 | National Natural Science Foundation of China |
| 源URL | [http://ir.imr.ac.cn/handle/321006/105252]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Dong Junhua |
| 作者单位 | Chinese Acad Sci, Inst Met Res, Shenyang 110016, Peoples R China |
| 推荐引用方式 GB/T 7714 | Yang Jingfeng,Dong Junhua,Ke Wei,et al. INFLUENCE OF pH VALUES AND CORROSION PRODUCTS ON LOW CARBON STEEL CORROSION SUSCEPTIBILITY IN BORATE BUFFER SOLUTION[J]. ACTA METALLURGICA SINICA,2011,47(2):152-156. |
| APA | Yang Jingfeng,Dong Junhua,Ke Wei,&Chen Nan.(2011).INFLUENCE OF pH VALUES AND CORROSION PRODUCTS ON LOW CARBON STEEL CORROSION SUSCEPTIBILITY IN BORATE BUFFER SOLUTION.ACTA METALLURGICA SINICA,47(2),152-156. |
| MLA | Yang Jingfeng,et al."INFLUENCE OF pH VALUES AND CORROSION PRODUCTS ON LOW CARBON STEEL CORROSION SUSCEPTIBILITY IN BORATE BUFFER SOLUTION".ACTA METALLURGICA SINICA 47.2(2011):152-156. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。