MICROSTRUCTURE NEAR SCRATCH ON ALLOY 690TT AND STRESS CORROSION INDUCED BY SCRATCHING
文献类型：期刊论文
| 作者 | Meng Fanjiang1; Wang Jianqiu1; Han En-Hou1; Shoji, Testuo2; Ke Wei1 |
| 刊名 | ACTA METALLURGICA SINICA
 |
| 出版日期 | 2011-07-11 |
| 卷号 | 47期号:7页码:839-846 |
| 关键词 | Ni base alloy 690 surface scratch microstructure stress corrosion cracking |
| ISSN号 | 0412-1961 |
| DOI | 10.3724/SP.J.1037.2011.00213 |
| 通讯作者 | Wang Jianqiu(wangjianqiu@imr.ac.cn) |
| 英文摘要 | The microstructure and stress corrosion cracking (SCC) behavior of scratched zone on alloy 690TT were studied by using rnicrohardness, TEM, EBSD-OIM and immersion experiment in caustic solution. It was found that a deformed hardening layer with a dimension range of 100 Am was produced near the scratch. TEM and EBSD-OIM observations showed that the grains at shallow surface of scratch groove were refined to nano size. SCC tests for scratched alloy 690TT were performed in caustic solution at high temperature with or without addition of lead oxides. The results showed that SCC cracks initiated and propagated at scratch banks and scratch grooves. Grain boundaries, twin boundaries deformed and microcracks produced during scratching process are preferential sites for SCC. The oxide films formed on scratch groove were loosed by lead. The SCC crack length increased with increase of lead content. Scratched alloy 690TT is susceptible to SCC. |
| 资助项目 | National Basic Research Program of China[2006CB605000] |
| WOS研究方向 | Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| WOS记录号 | WOS:000294980700012 |
| 出版者 | SCIENCE PRESS |
| 资助机构 | National Basic Research Program of China |
| 源URL | [http://ir.imr.ac.cn/handle/321006/105952]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Wang Jianqiu |
| 作者单位 | 1.Chinese Acad Sci, Inst Met Res, State Key Lab Corros & Protect, Shenyang 110016, Peoples R China 2.Tohoku Univ, Fracture & Reliabil Res Inst, Sendai, Miyagi 9808579, Japan |
| 推荐引用方式 GB/T 7714 | Meng Fanjiang,Wang Jianqiu,Han En-Hou,et al. MICROSTRUCTURE NEAR SCRATCH ON ALLOY 690TT AND STRESS CORROSION INDUCED BY SCRATCHING[J]. ACTA METALLURGICA SINICA,2011,47(7):839-846. |
| APA | Meng Fanjiang,Wang Jianqiu,Han En-Hou,Shoji, Testuo,&Ke Wei.(2011).MICROSTRUCTURE NEAR SCRATCH ON ALLOY 690TT AND STRESS CORROSION INDUCED BY SCRATCHING.ACTA METALLURGICA SINICA,47(7),839-846. |
| MLA | Meng Fanjiang,et al."MICROSTRUCTURE NEAR SCRATCH ON ALLOY 690TT AND STRESS CORROSION INDUCED BY SCRATCHING".ACTA METALLURGICA SINICA 47.7(2011):839-846. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。