Corrosion behaviour of carbon steel in different concentrations of HCl solutions containing H2S at 90 degrees C
文献类型：期刊论文
| 作者 | Tang, Junwen2; Shao, Yawei1,2; Zhang, Tao1,2; Meng, Guozhe1,2; Wang, Fuhui1,2 |
| 刊名 | CORROSION SCIENCE
 |
| 出版日期 | 2011-05-01 |
| 卷号 | 53期号:5页码:1715-1723 |
| 关键词 | Steel Weight loss EIS SEM XRD Acid corrosion |
| ISSN号 | 0010-938X |
| DOI | 10.1016/j.corsci.2011.01.041 |
| 通讯作者 | Shao, Yawei(shaoyawei@hrbeu.edu.cn) |
| 英文摘要 | The corrosion behavior of SAE-1020 carbon steel in H2S-containing solutions with different concentration of HCl at 90 degrees C was investigated by weight loss, electrochemical measurements, SEM and XRD analysis. The results showed that the corrosion rate of carbon steel increased with increasing HCl concentration. Uniform corrosion was found on the carbon steel surface in H2S + HCl solutions, while corrosion cavities were observed in the solution only containing H2S. The ratio of Faradaic process of total corrosion process increased with the increase of HCl concentration. The corrosion products were solely composed of mackinawite in the H2S-containing solutions with or without HCl. (c) 2011 Elsevier Ltd. All rights reserved. |
| 资助项目 | academe of Lanzhou Petrochemical Company ; CNPC ; University of China[NCET-09-0052] ; Fundamental Research Funds for the Central Universities[HEUCFZ1019] |
| WOS研究方向 | Materials Science ; Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| WOS记录号 | WOS:000289866400012 |
| 出版者 | PERGAMON-ELSEVIER SCIENCE LTD |
| 资助机构 | academe of Lanzhou Petrochemical Company ; CNPC ; University of China ; Fundamental Research Funds for the Central Universities |
| 源URL | [http://ir.imr.ac.cn/handle/321006/106295]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Shao, Yawei |
| 作者单位 | 1.Chinese Acad Sci, State Key Lab Corros & Protect, Inst Met Res, Shenyang 110015, Peoples R China 2.Harbin Engn Univ, Corros & Protect Lab, Key Lab Supertight Mat & Surface Technol, Minist Educ, Harbin 150001, Peoples R China |
| 推荐引用方式 GB/T 7714 | Tang, Junwen,Shao, Yawei,Zhang, Tao,et al. Corrosion behaviour of carbon steel in different concentrations of HCl solutions containing H2S at 90 degrees C[J]. CORROSION SCIENCE,2011,53(5):1715-1723. |
| APA | Tang, Junwen,Shao, Yawei,Zhang, Tao,Meng, Guozhe,&Wang, Fuhui.(2011).Corrosion behaviour of carbon steel in different concentrations of HCl solutions containing H2S at 90 degrees C.CORROSION SCIENCE,53(5),1715-1723. |
| MLA | Tang, Junwen,et al."Corrosion behaviour of carbon steel in different concentrations of HCl solutions containing H2S at 90 degrees C".CORROSION SCIENCE 53.5(2011):1715-1723. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。