CHARACTERIZATION OF TiAl PRE-ALLOYED POWDER AND ITS DENSIFICATION MICROSTRUCTURE
文献类型：期刊论文
| 作者 | Wang Gang; Zheng Zhuo; Chang Litao; Xu Lei; Cui Yuyou; Yang Rui |
| 刊名 | ACTA METALLURGICA SINICA
 |
| 出版日期 | 2011-10-11 |
| 卷号 | 47期号:10页码:1263-1269 |
| 关键词 | TiAl gas atomization metastable phase rnicrosegregation |
| ISSN号 | 0412-1961 |
| DOI | 10.3724/SP.J.1037.2011.00136 |
| 通讯作者 | Cui Yuyou(yycui@imr.ac.cn) |
| 英文摘要 | TiAl pre-alloyed powder (nominal composition Ti-47Al-2Cr-2Nb-0.2W-0.15B, atomic fraction, %) was produced by electrode induction melting gas atomization (EIGA) technique. The average diameter is 120.7 mu m, and the distribution of the powder diameter follows Gaussian distribution. The phase constitution is a function of particle diameter. The amount of the gamma phase increases with powder diameter increasing, the finest powder consists of predominantly alpha(2) phase. The alpha(2) phase in the powder was transformed into gamma phase after annealing at temperatures higher than 500 degrees C. Local coarsening was observed in the microstructure of TiAl compact duo to the microsegregation of elements in the powder. The)(PS result indicated that the outer layer of the TiAl pre-alloyed particle consists of a thin layer of Al(2)O(3) and TiO(2). |
| WOS研究方向 | Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| WOS记录号 | WOS:000298903300007 |
| 出版者 | SCIENCE PRESS |
| 源URL | [http://ir.imr.ac.cn/handle/321006/106415]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Cui Yuyou |
| 作者单位 | Chinese Acad Sci, Inst Met Res, Shenyang 110016, Peoples R China |
| 推荐引用方式 GB/T 7714 | Wang Gang,Zheng Zhuo,Chang Litao,et al. CHARACTERIZATION OF TiAl PRE-ALLOYED POWDER AND ITS DENSIFICATION MICROSTRUCTURE[J]. ACTA METALLURGICA SINICA,2011,47(10):1263-1269. |
| APA | Wang Gang,Zheng Zhuo,Chang Litao,Xu Lei,Cui Yuyou,&Yang Rui.(2011).CHARACTERIZATION OF TiAl PRE-ALLOYED POWDER AND ITS DENSIFICATION MICROSTRUCTURE.ACTA METALLURGICA SINICA,47(10),1263-1269. |
| MLA | Wang Gang,et al."CHARACTERIZATION OF TiAl PRE-ALLOYED POWDER AND ITS DENSIFICATION MICROSTRUCTURE".ACTA METALLURGICA SINICA 47.10(2011):1263-1269. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。